Abstract:The corrosion behavior of the 70/30 Cu–Ni alloy in stagnant, aerated pristine and sulfide-containing simulated seawater as a function of exposure time was investigated with polarization curve measurement and electrochemical impedance spectroscopy (EIS). It was demonstrated that the compact protective oxide film formed on the 70/30 Cu–Ni alloy resulted in the decrease of corrosion rate in aerated pristine seawater; while the corrosion rate of 70/30 Cu–Ni alloy in aerated sulfide-containing seawater increased dramatically due to the catalysis of the sulfide ions or sulfide scale for both the cathodic and anodic reactions. The impedance spectra and the corresponding equivalent circuits confirmed that a duplex layer of a surface film was formed on the 70/30 Cu–Ni alloy in aerated pristine seawater after a period of time and that the inner layer was responsible for the good resistance of the alloy; while only a porous and non-protective corrosion product layer formed on the 70/30 Cu–Ni alloy in aerated sulfide-containing seawater, which made small values of charge transfer resistance (Rct) to last for a abnormally long time by interfering with the growth of the protective oxide film. The composition of the surface film on the alloy in pristine and sulfide-containing seawater for different exposure times were investigated thoroughly by XPS. It was found that the duplex corrosion product layer formed on the alloy in pristine seawater was composed of an inner Cu2O and an outer CuO layer. The porous and non-protective corrosion product layer formed on the alloy in aerated sulfide-containing seawater was a mixture of CuCl, Cu2S, NiS, Cu2O and NiO with trace amounts of CuO and Ni(OH)2 and that the most significant component was Cu2S. In addition, SEM was used to analyze the topography of the 70/30 Cu–Ni alloy in both solutions after different exposure times.

Influence of Deformation and Heat Treatment on Seawater Corrosion of 70Cu-30Ni Alloy

Microstructure and Corrosion Resistance of Medical Cobalt-Based Alloys

Correlation of Seawater Corrosion and Processing of Cu Ni Alloy Tubes

Relationship of Corrosion Product Films and Recrystallization of 70Cu-30Ni Alloy

Characteristics and Formation of Corrosion Product Films of 70cu–30ni Alloy in Seawater

Seawater corrosion of A Cu-Ni alloy in intermittent immersion

PROCESS OF FORMATION OF CORROSION FILMS ON ALLOY 70Cu-30Ni IN SEAWATER

Effect of Thermo-Mechanical Treatments on Corrosion Behavior of Cu-15Ni-8Sn Alloy in 3.5 Wt% NaCl Solution

Effect of Annealing on Microstructure and Properties of Cu–30Ni Alloy Tube

Corrosion Behavior of Novel Cu–Ni–Al–Si Alloy with Super-High Strength in 3.5% NaCl Solution

Corrosion and corrosive-wear behaviors of a high strength and toughness Cu-15Ni-8Sn alloy in seawater

Long-Term Corrosion Behavior of Cu-10Ni and Cu-20Ni Alloys in Simulated Seawater

Accelerated Corrosion Behavior Of B10 Cu-Ni Alloy In Seawater

The Corrosion Behavior of Cu-Ni-Si Alloy in Sea Water with Deep-Sea Bacteria

Effect of Aging Time on the Corrosion Behavior of a Cu-Ni-Si Alloy in 3.5 wt% NaCl Solution

Effect of heat treatment on corrosion resistance of 00Ni40Cu3 stainless steel

Surface characterization and corrosion behavior of 70/30 Cu–Ni alloy in pristine and sulfide-containing simulated seawater

Effect of cold deformation on the corrosion behavior of ZrTiNb alloys in an anodic environment of proton exchange membrane water electrolysis

Effects of Al addition on corrosion behavior and mechanical property of high-strength and high-elasticity Cu-20Ni-20Mn-0.3Nb-0.3Cr-0.3Zr alloy

Effects of Aging Treatment on Corrosion Behavior of a Tensile Deformed Al-Cu-Mn-Fe-Zr Alloy in 3.5% NaCl Solution

ELECTROCHEMICAL CORROSION BEHAVIOR OF 90/10 Cu-Ni ALLOY IN FLOWING SEAWATER