Abstract:The influence of temperature and strain rate on the hot tensile properties of 0Cr18AlSi ferritic stainless steel, a potential structural material in the ultra-supercritical generation industry, was investigated at temperatures ranging from 873 to 1123 K and strain rates of 1.7 × 10−4–1.7 × 10−2 s−1. The microstructural evolution linked to the hot deformation mechanism was characterized by electron backscatter diffraction (EBSD). At the same strain rate, the yield strength and ultimate tensile strength decrease rapidly from 873 K to 1023 K and then gradually to 1123 K. Meanwhile, both yield strength and ultimate tensile strength increase with the increase in strain rate. At high temperatures and low strain rates, the prolonged necking deformation can be observed, which determines the ductility of the steel to some extent. The maximum elongation is obtained at 1023 K for the strain rates of 1.7 × 10−3 and 1.7 × 10−2 s−1, while this temperature is postponed to 1073 K once decreasing the strain rate to 1.7 × 10−4 s−1. Dynamic recovery (DRV) and continuous dynamic recrystallization (CDRX) are found to be the main softening mechanisms during the hot tensile deformation. With the increase of temperature and the decrease of strain rate (i.e., 1123 K and 1.7 × 10−4 s−1), the sub-grain coalescence becomes the main mode of CDRX that evolved from the sub-grain rotation. The gradual decrease in strength above 1023 K is related to the limited increase of dynamic recrystallization and the sufficient DRV. The area around the new small recrystallized grains on the coarse grain boundaries provides the nucleation site for cavity, which generally results in a reduction in ductility. Constitutive analysis shows that the stress exponent and the deformation activation energy are 5.9 and 355 kJ·mol−1 respectively, indicating that the dominant deformation mechanism is the dislocations motion controlled by climb. This work makes a deeply understanding of the hot deformation behavior and its mechanism of the Al-bearing ferritic stainless steel and thus provides a basal design consideration for its extensive application.

Deformation behaviour of an FeAl Intermetallic alloy at elevated temperatures

The Mechanical Properties of Fe-36.5Al and Its Cr or Ti Containing Alloys at Elevated Temperature

Enhanced ductility in coarse grained Fe3Al alloys

Study of Superplastic Deformation in an FeAl Based Alloy with Large Grains

Deformation mechanisms of Al0.1CoCrFeNi at elevated temperatures

Thermal Performance Determination of Binary Fe-Al Alloys at Elevated Temperatures

Microstructure Evolution of a Fe3Al-based Alloy with Coarse Initial Grains Deformed at Elevated Temperature

On Phenomenon Of Superplasticity In Fe3al With Large Grains

SUPERPLASTICITY IN LARGE-GRAINED Fe-36.5Al BASED ALLOYS ADDED Ti

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

THE SUPERPLASTICITY OF Fe-28Al-5Cr AND Fe-28Al-5Cr-0.5Nb-0.1C ALLOYS

Dynamic Restoration Mechanism of a Fe<sub>3</sub>Al Based Alloy During Elevated Temperature Deformation

Low Temperature Superplasticity in Fe3Al Alloys

Dynamic Restoration Mechanism of a Fe3Al Based Alloy During Elevated Temperature Deformation

High temperature deformation mechanism and microstructural evolution of relatively lightweight AlCoCrFeNi high entropy alloy

Anomalous Increase of Fracture Toughness of TiAl-based Alloys at High Temperature

High Tensile Elongation of a Directionally Solidified NiAl Multiphase Alloy at High Temperatures

Tensile Properties and Microstructural Evolution of an Al-Bearing Ferritic Stainless Steel at Elevated Temperatures

Temperature Dependence of Deformation Behaviour and Dislocation Structure of Al67Mn8Ti26 L12 Intermetallic Alloy

High Temperature Deformation Characteristics of an Alumina‐Forming Stainless Steel