Abstract:The present article is dedicated to the microstructural characterization of the surface layer of two different austenitic stainless steels, 304L and 904L, subjected to a low-temperature carburizing process (Kolsterising®, Bodycote) and a subsequent annealing at high-temperature. The carburizing treatment forms a hard expanded austenite in both materials. However, thermal decomposition occurs at high temperatures through precipitation of chromium-carbides, hence compromising the surface hardness of the treated materials.The purpose of this paper is to explore the potential applicability of electron backscatter diffraction (EBSD) technique to reveal the correlation between phase transformation and hardness. First of all, EBSD was used to create kernel average misorientation (KAM) maps of the modified surface layers to identify the internal strains. Moreover, the preferential sites for precipitation of chromium-compound during annealing were identified. We prove here that EBSD can provide useful information to distinguish the main hardening mechanisms within modified surface layers at different annealing conditions. When combined with nano-indentation, X-ray diffraction (XRD) and glow discharge optical emission spectrometry (GDOES), an effective bridge between macro and microanalysis can be obtained. Solid solution hardening was found to be the dominant mechanism in as-carburized materials, with pre-existing strain promoting a higher supersaturation. In the annealed materials, the alloy composition and surface finish can also dictate the preferential sites of precipitation and can therefore affect the residual hardening.

Observation and Analysis of the Microstructure in Carburized Surface Layer of Steel 20Cr2Ni4A Treated with Conventional and Rare Earth Carburizing Processes

Microstructure Evolution and Mechanical Properties of High-Temperature Carburized 18Cr2Ni4WA Steel

Microstructures and Mechanical Properties of Surface and Center of Carburizing 23cr2ni2si1mo Steel Subjected to Low-Temperature Austempering

Gradient microstructure evolution and hardening mechanism of carburized steel under novel heat treatment

Preparation and Microstructure of Hard Bainite in Surface Layer of Carburized 20crmnmoal Steel

Effect of Carbon Concentration Gradient on Multi-Level Composite Microstructure and Performance of M50NiL Steel

Carburization-induced microstructure evolution and hardening mechanism of 18CrNiMo7-6 steel

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment

Microstructure and Wear Property of Carbon Nanotube Carburizing Carbon Steel by Laser Surface Remelting

Optimization of heat treatment process after vacuum carburizing of 18Cr2Ni4WA steel

Thermodynamics of Phase Transformation and Microstructure Evolution of 18Cr2Ni4WA Carburized Steel during High‐Temperature Tempering

Effect of microstructure on wear resistance during high temperature carburization heat treatment of heavy-duty gear steel

Characterization of the Microstructure and Hardness of Case-Carburized Gear Steel.

Compositional and structural characterization of alloyed carbide by 3D atom probe and high-resolution TEM

Experimental Study on the Influence of Surface Carbon Content on Crack Initiation for 20Cr2Ni4A Steel

Fabrication and mechanical properties of micro/nano-crystalline layers in M50NiL carburized steel

Carburization Induced Extra-Long Rolling Contact Fatigue Life of High Carbon Bearing Steel

Effect of Short-Time Carburizing Treatment on Microstructure and Mechanical Properties of M50 Steel

Understanding the microstructure-properties relationship of low-temperature carburized austenitic stainless steels through EBSD analysis