Abstract:The electrochromic films featuring the well dispersed ITO nanocrystal (about 10 nm) in amorphous WO3 (ITO@WO3) have been successfully fabricated with a solution process. The structure and electrochromic properties of the as-prepared films were studied by high resolution transmission electron microscope, scanning electron microscope, X-ray photoelectron spectroscopy, X-ray diffraction, and electrochemical methods. The measured coloration/bleach time decreases from 10.5/27.8 s to 5.7/0.9 s with the increasing of ITO/AMT ratio indicating that embedded ITO nanocrystals induce the nanocrystal/glassy interface effect remarkably improving the ion diffusion coefficient and electrochemical activity. The optimal Delta T at 633 nm of 0.1 ITO@WO3 films is about 53.80% much higher than that of pure WO3 (about 42.09%). But in near-infrared (NIR) range the pure WO3 films show the best transmittance modulation rather than the composite films. The above stated results are indicative that the interface effects of embedded ITO nanocrystals play the key role while its plasmon-induced electrochromic effects are limited because of not only excellent NIR modulation capability of amorphous WO3 itself but also the relative large size of ITO nanocrystals used, demonstrating that smaller nanocrystal size (similar to 5 nm) are required for better electrochromic performance of the composite films. (C) 2019 The Electrochemical Society.

Electrochemical and electrochromic properties of MoO3 thin film

Electrochromism of titanium oxide thin films

Effect of annealing temperature on the structure and electrochromic properties of MoO3 thin films

STUDY ON ELECTROCHROMIC PERFORMANCES OF AMORPHOUS MoO3 FILMS PREPARED AT ULTRACOLD TEMPERATURE

Time-resolved electrochromic properties of MoO 3 thin films electrodeposited on a flexible substrate

Properties of Electrochromic MoO3 Thin Films on Plastic Substrate

Electrochromic Response Time of MoO3 Film Fabricated by Reactive Sputtering

Electrochemical study of MoO3 and MoO3:Li+ thin films: the influence of lithium ions

Study on structural and optical properties of thermally evaporated MoO3 thin films

A Novel Inorganic Ion Conductor Electrochromic Device: MoO<sub>3</sub>/LiAlO<sub>2</sub>/NiO<sub>x</sub>

Electrochromic Properties of WO<sub>3</sub> Thin Films Deposited on ITO/PET Substrates by Glancing Angle Magnetron Sputtering

Electrochromic composites films composed of MoO 3 doped by tungsten atoms with remarkable response speed and color rendering efficiency via electrochemical deposition

Improvement of Electrochromic Performance by Embedding ITO Nanocrystals in Amorphous WO3 Film

Influence of annealing on microstructure and electrochromic properties of WO3 thin film

Properties of MoO3 Films Deposited by Electron Beam Evaporation

Printing of WO3/ITO Nanocomposite Electrochromic Smart Windows

Electrochromic Properties of WOx-Mo thin films on polyethylene terephthalates soft substrate

Magnetic, Optical and I-V Characteristics of MoO3 thin films

Novel transparent conductive films In2O3:Mo

Electrochromic coloration of single-layer ITO:Nb oxides thin film

Preparation and Characterization of Tungsten Oxide Thin Films with High Electrochromic Performance