Abstract:Amorphous Fe73.5-xCoxSi13.5B9Cu1Nb3（x=10,30,50） ribbons were prepared by the single copper wheel melt spinning technique in the air atmosphere.The nanocrystallization kinetics of amorphous ribbons was investigated by differential scanning calorimetry（DSC）.The apparent activation energies of amorphous ribbons were calculated by using Kissinger and Ozawa methods.It was found that the activation energies of the first crystallization reduce and those of the second crystallization rise with increasing Co content.The local Avrami parameter m for primary crystallization was calculated using Johnson-Mehl-Avrami（JMA） model.The values of the Avrami parameter showed that the primary crystallization mechanism of amorphous ribbons varied at different stages.In the initial stage,the crystallization mechanism was bulk crystallization with three dimensional nucleation and grain growth controlled by diffusion.In the following stage,it was surface crystallization with one dimensional nucleation and grain growth at a near zero nucleation rate.The variation of soft magnetic properties of nanocrystalline Fe63.5Co10Si13.5B9Cu1Nb3 powder cores as a function of milling time has been investigated.It was found that the effective permeability of the cores shows high frequency stability and decreases with increasing milling time.The quality factor increases with increasing frequency in the lower frequency range,reaches a maximum at the frequency of 80 kHz,and then decreases gradually with increasing frequency.

Magnetic Properties of Amorphous Co98−xZrxB2 Alloys Before and after Crystallization

Fe65B22Nd9Mo4 bulk nanocomposite permanent magnets produced by crystallizing amorphous precursors

High-temperature Magnetic Properties of Fe-based Nanocrystalline Alloy

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Annealing Temperature Dependance of Magnetic Properties and Magneto-Impedance Effect in CoZrB Alloys

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Magnetic Properties of Amorphous Nd2(Fe1−xCox)23

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Temperature Dependence of Magnetic Property for Glass-Coated Metal Microwires

Magnetic properties and nanocrystallization behavior of Co-based amorphous alloy

Magnetic properties evolution and crystallization behaviour of vacuum- and air-long-term-annealed rapidly quenched Fe80.3Co5Cu0.7B14 alloy

Magnetic properties of amorphous Co$_x$Nb$_{100-x}$ alloys produced by mechanical alloying

Crystallization and Soft Magnetic Behavior of Fe85.6−Mo Zr3.3Nb3.3B6.8Cu1 Alloys

Fe-B-Si-C-Cu amorphous and nanocrystalline alloys with ultrahigh hardness and enhanced soft magnetic properties

Fabrication and Soft Magnetic Properties of Fe–B–Si–Zr/Hf–Cu Nanocrystalline Alloys with High Glass-Forming Ability

Magnetic and Magneto-Caloric Properties of the Amorphous Fe92−xZr8Bx Ribbons

Unexpected magnetic behavior in amorphous Co90Sc10 alloy

Thermal and magnetic properties of Fe(Co)BCCu amorphous alloys with high saturation magnetization of 1.77 T

Magnetic properties of the composition of nanocrystals and amorphous matrix in an alloy of the Fe-Nb-Si-B-Cu system

Microstructure, crystallization behavior, and soft magnetic properties of Co-doped Finemet-type nanocrystalline alloys

Comprehensive study of the crystallization behavior, thermal stability, and magnetic properties of Co66.5Si15.5B12Fe4Ni2 amorphous ribbon