Abstract:Combined experimental and simulation analysis of bending failure of GLARE laminates. GLARE laminate experiences multiple damage modes during bending failure, including fiber fracture, matrix cracking, interlayer delamination, and fracture of aluminum alloy. In most cases, two or more failure modes occur together, which makes the damage process complex and unpredictable. This paper proposes a combination of experimental testing and numerical simulation to investigate the influence of fiber lay‐up direction and center open‐hole on the bending failure behavior of GLARE laminate. Simultaneously, Acoustic Emission (AE) technology was used to monitor the bending process of GLARE laminates in real‐time, and a numerical simulation model for the three‐point bending of GLARE laminates was established. The experimental results showed that the bending strength of intact specimens decreased significantly with the increase of the fiber off‐axis angle, whereas the strength retention of open‐hole specimens increased significantly with the increase of the fiber off‐axis angle. Based on the K‐means++ clustering algorithm, the peak frequencies corresponding to different damage modes of GLARE laminates were identified as follows: aluminum alloy damage [1–70 kHz], matrix cracking [93–210 kHz], interlaminar delamination [211–304 kHz], and fiber breakage [304–516 kHz]. The simulation results agreed well with the experimental results, showing that the damage in intact specimens initiated at the laminate edges and propagated sequentially along the thickness direction, while the damage in open‐hole specimens initiated at the hole edges and then propagated towards the laminate edges. Highlights The present study investigated the effects of fiber lay‐up direction and central open‐hole on the bending performance and failure behavior of GLARE laminate. In‐situ monitoring of the GLARE laminate during three‐point bending was conducted using AE technology. A model for simulating the progressive damage of GLARE laminate was established and its accuracy was verified.

Experimental study of bending behavior in CALL hybrid composites

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Computational modelling of postbuckling behavior of composite T-stiffened panels with different bonding methods

Experimental Investigation on Deformation and Strength of Carbon/epoxy Laminated Curved Beams

Failure behavior and damage visualization of thick carbon/aramid hybrid woven composites under flexural loading conditions

Experiment Study of Stiffness Degradation for Damaged Composite Laminates

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

Experimental and numerical characterization of flexural properties and failure behavior of CFRP/Al laminates

Energy dissipation theory performance of different layup patterns CFRP/aluminium alloy hat-shaped hybrid beams under three-point bending conditions

A Study on the Intralaminar Damage and Interlaminar Delamination of Carbon Fiber Composite Laminates under Three-Point Bending Using Acoustic Emission

Flexural progressive damage and failure behavior of carbon-aramid/epoxy hybrid woven composites

Transverse Bending and Axial Compressing Mechanical Characteristics of Carbon Fiber Reinforced Plastic Sandwich Laminated Square Tubes

Flexural Behavior of Hybrid Composite Beams with a Bamboo Layer and Lattice Ribs

Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM

Comparison on mechanical properties, damage evolution and aging effects of multi-delaminated composites under three point bending

Progressive Damage Behaviour Analysis and Comparison with 2D/3D Hashin Failure Models on Carbon Fibre-Reinforced Aluminium Laminates

A Combined Experimental and Computational Analysis of Failure Mechanisms in Open-Hole Cross-ply Laminates under Flexural Loading

Bending damage behavior of 3D-C/C-TiC-Cu composite based on acoustic emission technology

3D FEA Modelling of Laminated Composites in Bending and Their Failure Mechanisms

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Micro-XCT Characterization and Numerical Analysis of Bending Damage Mechanism in Carbon Fiber Plain, Twill and Winding Composite Tubes