Hot Chlorination Corrosion of Metallic Nickel by Chlorine Catalyzed by Sodium Chloride
Yuanyuan Chen,Shaobo Shen,Jinlang Gu,Zhen Zhang,Na Li
DOI: https://doi.org/10.1021/acsomega.0c03486
IF: 4.1
2020-10-13
ACS Omega
Abstract:Reducing chlorine corrosion to metals at high temperatures is a big problem for many industrial processes. Some high Ni alloys such as Hastelloy C-276 (Ni > 50 wt %) have been widely used for this purpose. Chlorine and chlorides often coexisted in many industrial processes at high temperatures, such as some industrial incinerators and metallurgical furnaces. Thus, a comprehensive experimental investigation regarding the effect of NaCl on the chlorination corrosion of metallic nickel powder by chlorine at a high temperature was performed. It was more convenient to investigate the intrinsic chlorination mechanisms and kinetics of metallic Ni if Ni powder was used instead of a Ni plate. It was found that there existed a critical chlorination temperature of 450 °C for relative safe use of Ni-based alloy in the presence NaCl. The Ni chlorination in the presence of NaCl was increased with increasing temperature and reached a maximum of 97% at 700 °C, which was about 21% higher than that in the absence of NaCl. An anhydrous NiCl<sub>2</sub> was initially formed at about 700 °C during the chlorination process and then immediately reacted with NaCl to form a novel eutectic complex with a flaky shape, a melting point of 585 °C, and a simplified molecular formula of NiNa<sub>0.33</sub>Cl<sub>2.33</sub> based on X-ray diffraction (XRD), differential thermal analysis (DTA), scanning electronic microscopy (SEM), and chemical analysis with inductively coupled plasma atomic emission spectroscopy (ICP-AES). As a result, only the complex of NiNa<sub>0.33</sub>Cl<sub>2.33</sub> and NaCl was left in the chlorinated product. At 700 °C, the chlorinated product evaporated only in the form of complex NiNa<sub>0.33</sub>Cl<sub>2.33</sub> instead of individual NiCl<sub>2</sub> or NaCl. The chlorination mechanisms of metallic Ni at a high temperature, for example, 700 °C, in the presence of NaCl were as follows. Step 1: Formation of initial chlorinated solid product NiCl<sub>2</sub> (mp 1001 °C) at a high temperature; step 2: The NiCl<sub>2</sub> reacted with solid additive NaCl (mp 801 °C) to form a final liquid product NiNa<sub>0.33</sub>Cl<sub>2.33</sub> (mp 585 °C); step 3: External Cl<sub>2</sub>(g) was dissolved in the liquid product layer; step 4: The chlorine dissolved in the liquid product of NiNa<sub>0.33</sub>Cl<sub>2.33</sub> reacted with the unreacted Ni core. The external Cl<sub>2</sub>(g) passed through the liquid product NiNa<sub>0.33</sub>Cl<sub>2.33</sub> layer faster than the solid product NiCl<sub>2</sub> layer formed in the absence of NaCl. This resulted in 21% more chlorination corrosion of metallic Ni powder with NaCl addition than that without NaCl addition.This article has not yet been cited by other publications.
chemistry, multidisciplinary