Abstract:Nitrogen oxides (NOx) are a primary source of air pollutants from combustion of fossil fuels. Though Mn-Ce based catalysts exhibit superior low temperature activities, their water and SO2 tolerance is inferior to other metal oxide catalysts, due to their strong water adsorption and sulfate species formation tendency at low reaction temperatures. Herein, a confinement strategy was adopted to design and synthesize a novel Mn-Ce based catalyst for selective catalytic reduction of NOx with NH3. The confined MnCeOx catalyst was assembled with a simple one pot method, using a mesoporous zeolite (ZSM-5) as the shell and Mn-Ce oxides as the active core (MnCeOx@Z5). Owing to the zeolite shell's shielding effect and the synergy between the alumina-silica zeolite shell's acidic properties and the mixed oxide cores' redox properties, the novel MnCeOx@Z5 catalyst displayed enhanced water and SO2 resistance as compared to the MnCeOx supported on ZSM-5 (MnCeOx/Z5) and its precursor (MnCeOx@Al-SiO2). Evidently, the zeolite sheath hinders sulfate species formation, and this phenomenon was further investigated by in situ diffuse reflectance infrared Fourier transform spectroscopy (In situ DRIFTS). The novel shielding and acid-redox synergy effect/strategy adopted in this work can be applied to design other high performance deNOx catalysts for air pollution control.

Study on Performance of Transition Metal-Doped Catalysts for Denox at Low-Temperature

Transition Metal Doped MnOx-CeO2 Catalysts by Ultrasonic Immersing for Selective Catalytic Reduction of NO with NH3 at Low Temperature

DeNOx Performance and Characteristic Study for Transition Metals Doped Iron Based Catalysts

Low-temperature DeNOx Characteristics and Mechanism of the Fe-doped Modified CeMn Selective Catalytic Reduction Catalyst

Reaction and Characterization of Low-Temperature Effect of Transition Nanostructure Metal Codoped SCR Catalyst

Enhancing the Deno Performance of MnO /Ceo2-Zro2 Nanorod Catalyst for Low-Temperature NH3-SCR by TiO2 Modification

Significant Effects of Adding Mode on Low-Temperature De-NOx Performance and SO2 Resistance of a MnCeTiOx Catalyst Prepared by the Co-Precipitation Method

DeNOxperformance and resistance to H2O and SO2of Mn-Ce doped V-W/Ti catalyst at middle-low temperature

High Efficiency of Ce-Modified MnOx/TiO2-ZrO2-Based Low-Temperature Selective Catalytic Reduction Denitration Catalysts

Effect of Metal Ions Doping (M = Ti4+, Sn4+) on the Catalytic Performance of MnOx/CeO2 Catalyst for Low Temperature Selective Catalytic Reduction of NO with NH3

Performance Study for Low-temperature SCR Catalysts Based on Mn-Ce Prepared by Different Methods

Influence of Ho doping on the deNOx performance of Mn-Ce/TiO2 low temperature SCR catalyst

Low-temperature scr of no with nh3 on Mn-based catalysts modified with cerium

Low-temperature selective catalytic reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 monolith catalyst

Performances of Mn-Ce-Zr/γ-Al2O3 Catalyst for Low Temperature Selective Catalytic Reduction of NO

Influence of WO3 doping on properties of MnOx/TiO2 catalyst for low-temperature selective catalytic reduction of NOx by NH3

Novel shielding and synergy effects of Mn-Ce oxides confined in mesoporous zeolite for low temperature selective catalytic reduction of NOx with enhanced SO2/H2O tolerance

Experimental Study on NO Reduction and Hg0 Oxidation over Low Temperature SCR Catalyst

Comparative study on transition element doped Mn–Zr–Ti-oxides catalysts for the low-temperature selective catalytic reduction of NO with NH3

Effect of Bimetal Element Doping on the Low-Temperature Activity of Manganese-Based Catalysts for NH3-SCR

Influence of the Addition of Transition Metals (cr, Zr, Mo) on the Properties of MnO X –feo X Catalysts for Low-Temperature Selective Catalytic Reduction of NO X by Ammonia