Effects of doping Bi and Nd on the phase transition and electric properties of (Bi 1/2 Na 1/2 ) 0.94 Ba 0.06 TiO 3 ceramics

Xiaojuan Li,Peng Liu,Zengzhe Xi,Pinyang Fang,Wei Long,Xiaogang Zhao

DOI: https://doi.org/10.1007/s10832-013-9881-1

2013-01-01

Journal of Electroceramics

Abstract:(Bi 1/2 Na 1/2 ) 0.94 Ba 0.06 TiO 3 (BNBT6) ceramics with 3 wt.% Bi 2 O 3 and x wt.%Nd 2 O 3 ( x = 0, 1.5, 4.5, 6.0) doping were prepared by solid state reaction. The phase transition behaviors and electric properties of ceramics were investigated. The results showed that with doping of 3 wt.% Bi 2 O 3 , an antiferroelectric (AFE) phase was induced in ferroelectric BNBT6 ceramics at room temperature. It was attributed to disruption of the ferroelectric coupling between [BO 6 ] octahedra since the generation of A-site vacancies. The AFE (Bi 1/2 Na 1/2 ) 0.94 Ba 0.06 TiO 3 -3wt.%Bi 2 O 3 (BNBT6-3B) ceramics showed a high phase transition temperature ( T m ~ 320 °C), corresponding to the AFE - paraelectric (PE) phase transition. Low Nd 2 O 3 ( x = 1.5, 4.5) doping was helpful to strengthen the AFE phase of BNBT6-3B, while high Nd 2 O 3 ( x = 6.0) resulted in a stronger frequency dispersion due to the enhancement of A-site cation disorder. With increasing temperature, the ceramics with low Nd 2 O 3 underwent a relaxor AFE - AFE - PE phase transition, while only relaxor AFE - PE phase transition was presented in high Nd 2 O 3 -doped ceramics. An excellent dielectric properties ( ε max = 2916) was obtained in x = 1.5 sample.