Abstract:The mechanical behavior of two-dimensional (2D) carbon fiber reinforced silicon carbide (C/SiC) composites is investigated at both quasi-static and dynamic uniaxial compression under temperatures ranging from 293 to 1273K. Experimental results show that temperature and strain rate dramatically affect the compressive behavior of 2D C/SiC composites. If the temperature is below 873K, the compressive strength increases with rising temperature. The reason is that the release of thermal residual stress enhances the compressive strength and this enhancement is more significant than the strength degradation due to the high temperature induced oxidation. In contrast, when the temperature rises above 873K, the compressive strength decreases as temperature rises due to the stronger effect of oxidation induced strength degradation. Moreover, the degradation of compressive strength at strain rate of 10−4/s and temperatures above 873K is much more obvious than those at higher strain rates, and the strain rate sensitivity factor of compressive strength increases remarkably at temperature above 873K. Post-deformation observation shows that failure angles and fracture surfaces are also strongly dependent on testing temperature and strain rate. The change of interfacial strength at high strain rate or high temperature is responsible for the variations.

Effects of strain rate and temperature on compressive strength and fragment size of ZrB2-SiC-graphite composites

Dynamic Compressive Behavior of ZrB2‐Based Ceramic Composites at Room Temperature and 1073 K

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

High‐temperature tensile strength and fracture behavior of ZrB2‐SiC‐graphite composite

Compressive Behavior of C/SiC Composites over a Wide Range of Strain Rates and Temperatures

Effects of temperature and strain rate on impact compression behaviors of three-dimensional carbon fiber/epoxy braided composites

Strain Rate Effect on Mechanical Properties of 3D Needle-Punched C/C Composites at Different Temperatures

Deformability of a SiCw/6061Al composite during high strain rate compression at elevated temperatures

Effect of graphite flake on microstructure as well as mechanical properties and thermal shock resistance of ZrB2–SiC matrix ultrahigh temperature ceramics

Effect of strain rate on the tensile properties of mini-SiC/SiC composites

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Microstructure and high temperature mechanical properties of hot-pressed ZrB2-based composites

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

Influence of strain rate and temperature on the compressive deformation of a eutectic Al-Si alloy based composite reinforced with -Si3N 4 whisker

Influence of Strain Rate and Temperature on the Compressive Deformation of a Eutectic Al-Si Alloy Based Composite Reinforced with -Si3n4 Whisker

Flow stress behavior of 30ZrCP/W composite under high temperature compression deformation

Microstructure and Mechanical Properties of ZrB2–SiC Composites Prepared by Gelcasting and Pressureless Sintering

Compressive Deformation Behavior of a 30 Vol.%zrcp/w Composite at Temperatures of 1300–1600 °C

Microstructure and mechanical properties of hot pressed ZrB2–SiCp–ZrO2 composites

Strain rate effect on the mechanical properties of ZrB2-SiC ceramics characterized nanoindentation

The deformation behaviors of SiCp/7A04 composites at high temperatures