Abstract:Synthesis and consolidation of (Zr,Ti)C were investigated in the present work. ZrC–TiC powder mixture was synthesized at 1650°C for 90 min by the carbothermal method. The prepared powder mixture was hot‐pressed at 1800 C for 60 min under a pressure of 40Mpa and then heat‐treated at 2100 C for 60 min. There were ZrC‐rich and TiC‐rich phases together with zirconium oxide phases in powder mixture and hot‐pressed samples, while there were no oxide phases in the heat‐treated sample and only ZrC‐rich and TiC‐rich phases were present in the sample. The FESEM image of the fracture surface of the samples shows that the porosity of the samples decreases with increasing temperature. Relative density, microhardness, and flexural strength increased from 93.8% to 98.6%, from 15.26 to 21.41 GPa, and from 185.02 to 220.69 MPa, respectively, with increasing temperatures from 1800 C to 2100 C. In contrast to these properties, the fracture toughness of the samples was reduced from 3.71 to 3.47 MPa·m1/2. The investigation of oxidation behavior also showed that oxidation is influenced by oxygen diffusion and exhibits nonlinear behavior as a function of time. With increasing oxidation temperature of hot‐pressed and heat‐treated samples from 600 to 1000°C, parabolic oxidation rate constants (kp) increased from .267 to 11.793 and from .367 to 10.993, respectively.

Microstructure and mechanical properties of hot pressed ZrB2–SiCp–ZrO2 composites

Microstructure and high temperature mechanical properties of hot-pressed ZrB2-based composites

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

Microstructure and Mechanical Properties of Hot-Pressed ZrB2–SiC–ZrO2f Ceramics with Different Sintering Temperatures

Microstructure and mechanical properties of zirconia-toughened ZrB2–MoSi2 composites prepared by hot-pressing

Mechanical Properties and Toughening Mechanism of WC-doped ZrB2–ZrSi2 Ceramic Composites by Hot Pressing

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Study on Mechanical Properties of Hot Pressing Sintered Mullite-Zro2 Composites with Finite Element Method

Mechanical properties and thermal shock behavior of hot-pressed ZrB2–SiC–AlN composites

Study on Zrc-20vol.%Sicw Ultrahigh Temperature Ceramics by Hot Pressing

Reactive hot pressing of ZrB2-SiC composites

Microstructure and Properties of Hot Pressed Zr2(Al(Si))4C5/SiC Composites

Microstructure and mechanical properties of ZrB2–SiC–ZrO2f ceramic

Microstructure and Mechanical Properties of ZrC-SiC-C_g Ceramic Prepared by Hot Pressing

Reactive Hot Pressing and Sintering Characterization of ZrB2–SiC–ZrC Composites

Microstructure, Mechanical Properties and Oxidation Behavior of Reactive Hot-Pressed (Zr,Ti)B2-SiC-ZrC Composites

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Characterization of hot‐pressed ZrC–TiC composites

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Microstructure and Mechanical Properties of Zrb2-Based Composites Reinforced and Toughened by Zirconia

ZrC–ZrB2 matrix composites with enhanced toughness prepared by reactive hot pressing