Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

ZrC–ZrB2 matrix composites with enhanced toughness prepared by reactive hot pressing

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Dense Submicron-Sized ZrC – W Composite Produced by Reactive Melt in Fi Ltration at 1200 ° C

Preparation and characterization of high-toughness ZrB2/Mo composites by hot-pressing process

Preparation And Mechanical Properties Of Zrb2-Based Laminated Composites

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructure and mechanical property of B4C–SiC–CrB2 composites fabricated via reactive hot pressing

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Novel TiC-based composites with enhanced mechanical properties

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Microstructure And Mechanical Properties Of Zrb2-Based Composites With Laminated Structure

High-performance B4C matrix composites fabricated from the B4C–Si–CeO2 system via reactive hot pressing

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Microstructure, Mechanical Properties and Oxidation Behavior of Reactive Hot-Pressed (Zr,Ti)B2-SiC-ZrC Composites

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Toughness Mechanism of Layered ZrB2 Based Composite Ceramic

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

In situ reaction and solid solution induced hardening in (Ti,Zr)B 2 ‐(Zr,Ti)C composites

Processing and Properties of ZrB2-Cu Composites Sintered by Hot-Pressing Sintering