Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel
Rui Wang,Fenghao Li,Zhiqiang Yu,Yan Kang,Meng Li,Yong Hu,Haoran An,Jing Fan,Fang Miao,Yuhong Zhao,Juergen Eckert,Zhijie Yan
DOI: https://doi.org/10.1016/j.matdes.2023.112497
IF: 9.417
2023-01-01
Materials & Design
Abstract:Large eutectic carbides presenting in the matrix deteriorate the mechanical properties of high carbon martensitic stainless steel. In the present work, nitrogen-alloyed martensitic stainless steel with different C/N ratios were designed by partial substitution of C by N of 9Cr18Mo, and their microstructure and mechanical properties were investigated. The results show that, with increasing the content of N up to 0.15 wt% in the experimental steel, the quantity and the size of eutectic carbides decrease； and the net-work eutectic carbides are gradually eliminated. The microstructure of all the steels is composed of lath martensite, twin martensite and M23C6 carbides. With partial substitution of C by N, the morphology of martensite blocks evolves from a lath shape to a blocky one, the quantity of twin martensite increases, and the nano-scaled Cr2N nitrides precipitate in the martensite matrix. The steel containing 0.15 wt% N exhibits the hardness of 60.5 HRC, a fracture strength of 1900 MPa and an elongation rate of 1.6 % due to hot rolling and heat treatment, which is attributed to the refinement of carbides and grains, solid solution of C and N, as well as the dense dislocation.