Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructures and mechanical properties of Mg-6Li-6.5Gd-1Dy-2Zn alloys

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Microstructures and mechanical properties of Mg-6Gd-(2-4)Y-1Zn alloys

MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-(11-13)Gd-1Zn ALLOYS

Microstructures and Mechanical Properties of Mg–10Gd–6Y–2Zn–0.6Zr(wt.%) Alloy

Effects of Zn and Gd Contents and Their Ratios on Microstructure and Mechanical Properties of As-Cast and As-Extruded Mg−8Li Alloys

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

Microstructures and Mechanical Properties of Mg-Gd-Y-(Mn, Zr) Magnesium Alloys

Microstructure Evolution and Mechanical Properties of the Mg-Sm-Gd-Zn-Zr Alloy During Extrusion

Microstructure And Mechanical Properties Of Duplex Structured Mg-Li-Zn-Y Alloys

Microstructural Evolution and Mechanical Properties of As‐Cast and As‐Extruded Mg–14Li Alloy with Different Zn/Y and Zn/Gd Addition

Microstructure and Mechanical Properties of Extruded Mg–8.5Gd–2.3Y–1.8Ag–0.4Zr Alloy

Effect of Extrusion Parameters on Microstructure and Mechanical Properties of Mg-6Zn-1Mn-0.2Gd Alloy

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Microstructures and mechanical properties of as-cast Mg–5Y–3Nd–Zr–xGd (x=0, 2 and 4wt.%) alloys

Microstructures and Tensile Properties of Mg-6Gd-3Y-1.4Zn-0.4Zr Alloys

Microstructure and Mechanical Properties of Mg-2.6Sm-1.3Gd-0.6Zn-0.5Zr Alloy