Abstract:Mg–Zn–Y–Nd alloy was prepared by casting and hot extrusion. The microstructure and mechanical properties of OM, SEM, XRD, TEM, and tensile tests were investigated with casting and hot extruded alloys. The results demonstrate that in a casting Mg–Y–Nd–Zr alloy, the α-Mg matrix is separated into the cell structure by a discontinuously distributed coarse Mg24Y5/α-Mg eutectic structure and fine Mg12Nd particles. TEM analysis shows that the Mg12Nd and Mg24Y5 phases have the orientation of \( {\left[001\right]}_{{\mathrm{Mg}}_{12}\mathrm{Nd}}//{\left[0221\right]}_{\upalpha -\mathrm{Mg}} \), and \( {\left[111\right]}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left[0001\right]}_{\upalpha -\mathrm{Mg}} \) and \( {\left(10\overline{1}\right)}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left(10\overline{1}0\right)}_{\upalpha -\mathrm{Mg}} \), respectively. The hot extrusion separates the Mg24Y5/α-Mg eutectic structure into fragments and aligns fragmentary Mg24Y5 particles along the extrusion direction. The interaction of hot extrusion and strengthening particles refines the α-Mg matrix greatly. Moreover, large strains result in the stacking faults of the matrix. As compared to the casting alloy, the hot-extruded one exhibits high yield strength, ultimate tensile strength, and elongation, which should be ascribed to the grain fineness, optimum distribution of strengthening particles and multiple substructures.

Microstructure Evolution and Mechanical Properties of the Mg-Sm-Gd-Zn-Zr Alloy During Extrusion

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Numerical and Experimental Investigation on Hot Backward Extrusion Process of Mg-Gd-Y-Zn-Zr Magnesium Alloy

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of extrusion temperature on microstructure, mechanical properties, and deformation mechanism of Mg-2.5Er-0.6Zr alloy

Evolution of Microstructure, Mechanical Properties, and Corrosion Resistance of Mg–2.2Gd–2.2Zn–0.2Ca (wt%) Alloy by Extrusion at Various Temperatures

Microstructure evolution difference in Mg96.5Gd2.5Zn1 alloys extruded from as-cast and solution-treated states

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Microstructure, Non-Basal Texture and Strength-Ductility of Extruded Mg-6Bi-3Zn Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Effects of extrusion on the microstructure and mechanical properties of Mg–Zn–Gd alloy reinforced with quasicrystalline particles

Influence of Extrusion Temperature on Microstructure and Mechanical Properties of Mg-4Y-4Sm-0.5Zr Alloy

Effects of extrusion ratio and temperature on the microstructure and mechanical properties of Mg–Zn–Yb–Zr extrusion alloys

High Performance Mg Alloy with Designed Microstructure and Phases