Abstract:In this study, shot peening (SP) treatment was implemented on a duplex (austenite and ferrite) stainless steel. By using X-ray diffraction residual stress determination and line profile analysis, the residual stress (including macro- and microstress) and microstructure evolutions in the surface layer of the shot peened material were discussed. Results pointed out that the initial thermal stress state were compressive (-80 MPa) in alpha phase and tensile (90 MPa) in gamma phase owing to the different thermal expansion coefficients of the two phases. After SP, the nonreversible plastic deformation of the surface layer and the interior of bulk was the main cause of the macrostresses. SP introduced more compressive residual stress into the gamma phase, the maximum compressive stress in gamma phase was similar to 1.3 times larger than that in alpha phase (-912 vs. -717 MPa) and occurred deeper in the sample interior (similar to 75 vs. 10 mu m). The inhomogeneous partitioning of the plastic strains, which was ascribed to the difference of the relative strength and deformation mechanism between the phases, was the contributing cause of microstresses. The average microstresses in surface layer of shot peened alloy were tensile in alpha phase and compressive in gamma phase, the magnitude of which changed with depth since the phase-specific plastic deformation was also a function of depth. The quantitatively microstructural analysis indicated that more deformation was stored in the gamma phase, the microstrain and dislocation density at the surface in gamma phase were about four and 2.6 times larger than that in alpha phase (7.25 vs. 1.83 x 10(-3), 3.9 vs. 1.5 x 10(15) m(-2)), respectively. Microhardness measurements showed that SP-induced work hardening was more evident in austenite, the hardness of austenitic phase was found significantly higher than that of ferritic phase in near surface region.

Residual Stress Relaxation and Micro-Structural Development of the Surface Layer of 18Crnimo7-6 Steel after Shot Peening During Isothermal Annealing

Microstructural Evolution and Mechanical Response of the Surface of 18Crnimo7-6 Steel after Multistep Shot Peening During Annealing

Micro-structure and Surface Layer Properties of 18Crnimo7-6 Steel after Multistep Shot Peening

Effect Of Shot Peening On The Residual Stress And Mechanical Behaviour Of Low-Temperature And High-Temperature Annealed Martensitic Gear Steel 18crnimo7-6

Experimental Study on Macro- and Microstress State, Microstructural Evolution of Austenitic and Ferritic Steel Processed by Shot Peening

Shot Peening Treatment and Characterization of 18CrNiMo7-6 Steel after Carburizing and Quenching

Relation of Hardness with FWHM and Residual Stress of GCr15 Steel after Shot Peening

Surface Modification of 304 Steel Using Triple-Step Shot Peening

Investigation on the Thermostability of Residual Stress and Microstructure in Shot Peened SAF 2507 Duplex Stainless Steel

Influence of Annealing on the Shot-Peened Surface of Duplex Stainless Steel at Elevated Temperatures

The evolution of residual stress and microstructure in shot peened s30432 austenitic stainless steel at high temperatures

Microstructure Thermostability of Shot Peened Duplex Stainless Steel Surface Layer

Thermal Relaxation Behavior of Residual Stress and Microstructure in Shot Peened S30432 Steel at Elevated Temperatures

Residual Stress and Microstructure Characterization of 34crmo4 Steel Modified by Shot Peening

Determination of surface mechanical property and residual stress stability for shot-peened SAF2507 duplex stainless steel by in situ X-ray diffraction stress analysis

Evaluation of the Residual Stress and Microstructure Character in SAF 2507 Duplex Stainless Steel after Multiple Shot Peening Process

Thermal relaxation behavior of residual stress in laser hardened 17-4PH steel after shot peening treatment

Characterization on Surface Mechanical Properties of Ti–6Al–4V after Shot Peening

Thermostability of S30432 Shot Peened Surface Layer

Precipitation and Residual Stress Relaxation Kinetics in Shot-Peened Inconel 718

INVESTIGATION OF SURFACE GRADIENT MICROSTRUCTURE OF SHOT PEENED S30432 STEEL BY X-RAY LINE PROFILE ANALYSIS METHOD