Abstract:Inconel 718 has good fabricability, high strength at elevated temperatures, and high corrosion resistance and is widely deployed in many aerospace and other high-performance applications. With the molten pool's rapid solidification during laser powder bed fusion (LPBF), the resulting microstructures differ from those expected in equilibrium conditions. Residual stresses, microsegregation, anisotropy, undesirable phases, layered structure, and lower mechanical properties are the challenges that must be addressed before LPBF-ed Inconel 718 parts can be industrially implemented. Heat treatment of Inconel 718 after the LPBF process is widely discussed in the literature, and the proposed heat treatment processes do not address all the challenges mentioned above. For this reason, specific heat treatments should be designed to achieve desired mechanical properties. Four different high-temperature heat treatment procedures were developed and tested in recent work to study the effect of various heat treatment parameters on the type of precipitates, grain size, room and elevated temperature mechanical properties, and creep properties of LPBF-ed Inconel 718. Two heat treatment procedures were designed to study the effect of eliminating the stress relief cycle and increasing the soaking time of solution heat treatment at the same hot isostatic pressing (HIP) and aging conditions. The other two heat treatment procedures were designed to study the effect of stress relief and aging parameters, with similar HIP and solution annealing parameters. The investigated heat treatment procedures showed the formation of equiaxed grain size and a significant amount of γ ′′ particles at the grain boundary in addition to primary carbide types (MC). Three different grain sizes could be obtained, starting with the same as-built microstructure by controlling post-process heat treatment parameters. The first type, coarse grain size (ASTM grain size No. G 3), suitable for creep application, was achieved by increasing the soaking time at the aging cycle. The second type, the formation of serrated grain boundaries suitable for good fatigue and creep properties, was achieved by decreasing the stress relief cycle's soaking time and temperature. The third type, fine grain size (ASTM grain size No. G 6), which is preferable for fatigue properties, was achieved by decreasing the soaking time at the solution annealing cycle. Among the different heat treatment conditions, the heat treatment with lower stress relief temperature and longer soaking time at solution annealing steps showed compromised equiaxed grain size with serrated grain boundaries, and it was selected for mechanical testing. The mechanical properties at room and elevated temperature (650 °C) and creep properties under constant axial stress of 690 MPa at 650 °C until failure were evaluated. The obtained elongation is > 2 × higher than the available properties in the AMS 5663 for wrought Inconel 718, AMS 5383 for cast Inconel 718, and ASTM F3055 for LPBF while maintaining a higher tensile strength above the average level found in the standards. It can be concluded that the performed heat treatment achieves higher mechanical properties. The values of UTS, YS, elongation, and reduction of area percentages are similar in the Z and XY orientations, revealing the presence of isotropic microstructure and uniform distribution of MC and γ ′′ precipitates.

Precipitation and Residual Stress Relaxation Kinetics in Shot-Peened Inconel 718

Effect of Thermal Relaxation on Residual Stress and Microstructure in the Near-Surface Layers of Dual Shot Peened Inconel 625

Effect of Shot Peening on Residual Stress and Microstructure in the Deformed Layer of Inconel 625

Effect of shot peening with different peening intensity and coverage on surface integrity of Inconel 718 alloy

Precipitation kinetics of γ ′ and γ ′′ particles in Inconel 718 and its influence on mechanical properties

Study of Pre-Precipitated Δ Phase Promoting Deformation Twinning and Recrystallization Behavior of Inconel 718 Superalloy During Hot Compression

Nondestructive Evaluation of Residual Stress in Shot Peened Inconel Using Ultrasonic Minimum Reflection Measurement

Microstructure evolution of an Inconel 718 alloy prepared by electron beam smelting

Investigation on Surface Layers Characteristics of Pre-Stressed Shot Peening Inconel 625

Precipitation behavior during high-temperature isothermal compressive deformation of Inconel 718 alloy

Characterization of Precipitation in Gradient Inconel 718 Superalloy

Optimization of the Post-Heat Treatment of Additively Manufactured IN718

On the Residual Stress Relaxation in Inconel 718 Superalloys at High Temperature by Real-Time Neutron Diffraction

Surface Mechanical Property and Residual Stress Stability of Shot-Peened Mg-8Gd-3Y Alloy by In-Situ X-ray Diffraction

Revealing the γ′ and γ′′ Phase Fractions of Additively Manufactured and Differently Heat‐Treated Nickel‐Base Superalloy IN718 by Atom Probe Tomography and Their Impact on Mechanical Properties

Isothermal Solid‐State Transformations of Inconel 718 Alloy Fabricated by Selective Laser Melting

Residual Stress Relaxation and Micro-Structural Development of the Surface Layer of 18Crnimo7-6 Steel after Shot Peening During Isothermal Annealing

Development of the Microstructure and Mechanical Properties of Cold-Sprayed IN718 Alloy Coating by a Novel In-Situ Shot Peening Process

Simulations of the effect of shot peening backstress on nanoindentation

On the Deformation Induced Heterogeneous Precipitation of Γ″ Phase in Inconel 718 Alloy

The Precipitation Behavior Effect of Δ and Γ" Phases on Mechanical Properties of Laser Powder Bed Fusion Inconel 718 Alloy