Abstract:In order to investigate the influence of shot peening on microstructure of laser hardened steel and clarify how much influence of initial microstructure induced by laser hardening treatment on final microstructure of laser hardened steel after shot peening treatment, measurements of retained austenite, measurements of microhardness and microstructural analysis were carried out on three typical areas including laser hardened area, transitional area and matrix area of laser hardened 17-4PH steel. The results showed that shot peening was an efficient cold working method to eliminate the retained austenite on the surface of laser hardened samples. The surface hardness increased dramatically when shot peening treatments were carried out. The analyses of microstructure of laser hardened 17-4PH after shot peening treatment were carried out in matrix area and laser hardened area via Voigt method. With the increasing peening intensity, the influence depth of shot peening on hardness and microstructure increased but the surface hardness and microstructure did not change when certain peening intensity was reached. Influence depth of shot peening on hardness was larger than influence depth of shot peening on microstructure due to the kinetic energy loss along the depth during shot peening treatment. From the microstructural result, it can be shown that the shot peening treatment can influence the domain size and microstrain of treated samples but laser hardening treatment can only influence the microstrain of treated samples.

Thermal relaxation behavior of residual stress in laser hardened 17-4PH steel after shot peening treatment

Thermal Relaxation Behavior of Residual Stress and Microstructure in Shot Peened S30432 Steel at Elevated Temperatures

The evolution of residual stress and microstructure in shot peened s30432 austenitic stainless steel at high temperatures

Shot-Peened Surface Residual Stress Relaxation and Fatigue Resistance of 17-4PH Steel at Elevated Temperature

Influence of shot peening on the fatigue life of laser hardened 17-4PH steel

Residual Stress Field and Thermal Relaxation Behavior of Shot-Peened TC4-DT Titanium Alloy

Effect of shot peening on the microstructure of laser hardened 17-4PH

Residual Stress and Its Relaxation Behavior of TC4-DT Titanium Alloy after Shot Peening

Residual Stress Relaxation and Micro-Structural Development of the Surface Layer of 18Crnimo7-6 Steel after Shot Peening During Isothermal Annealing

Thermal Relaxation of Residual Stresses in Shot Peened Surface Layer on Tib2/Al Composite at Elevated Temperatures

The residual stress varying of shot peened TC4-DT titanium alloy

Effect of Thermal Relaxation on Residual Stress and Microstructure in the Near-Surface Layers of Dual Shot Peened Inconel 625

Influence of Annealing on the Shot-Peened Surface of Duplex Stainless Steel at Elevated Temperatures

Influence of Isothermal Annealing on Stress Relaxation of Shot Peened SiCw/Al Composite

Investigation on the Thermostability of Residual Stress and Microstructure in Shot Peened SAF 2507 Duplex Stainless Steel

Thermal Relaxation of Residual Stresses in Shot Peened Surface Layer of SiCw/Al Composite

Precipitation and Residual Stress Relaxation Kinetics in Shot-Peened Inconel 718

Thermal Stability of Residual Stresses and Work Hardening of Shot Peened Tungsten Cemented Carbide

Residual Stress Relaxation of Shot Peened Deformation Surface Layer on S30432 Austenite Steel under Applied Loading

The influence of shot peening process on the residual stress and microstructure in deformed surface layer of S30432 austenitic stainless steel

Calculation of Relaxation of Residual Stress and Change of Yield Strength in Shot Peened Layer