Abstract:In this article, we fabricated ZnO nanorod arrays on ITO substrates by cathodic electrodeposition method under different electrodeposition times. The XRD results illustrate that all of the peaks can be attributed to the hexagonal wurtzite structure. Besides, the crystallinity and the preferred c-axis orientation increase with longer electrodeposition time. With the increasing electrodeposition time, the diameter of nanorods, the surface roughness and thickness of ZnO nanorod arrays also increased. All samples exhibit hydrophobic behavior and the water contact angle (CA) increases to 120 degrees with the electrodeposition time increases to 120 min. After 10 min of ultraviolet (UV) irradiation, the wettability of the ZnO surfaces turn from hydrophobic to hydrophilicity, and the change of the CA reduction rate are 73.5, 63.5, 48.3 and 24.2%, corresponding to the sample electrodeposited 10, 30, 60 and 120 min, respectively. The intensity of UV emission peak ratio increases from 2.26 to 63.84% while the visible emission peak ratio decreases in PL spectra, which reveals defects decrease when electrodeposition time increases from 10 to 120 min. Raman spectrum shows three peaks which are located at 439, 566 and 1097 cm(-1), corresponding to the E-2, E-1L and E-3 mode of ZnO. (C) 2016 The Electrochemical Society. All rights reserved.

One-step electrodeposition of single-crystal ZnO nanotube arrays and their optical properties

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Effects of preparing conditions on controllable one-step electrodeposition of ZnO nanotube arrays

Controlled Growth of ZnO Array on FTO Glass Substrate by Electrodeposition

Seed layer-free electrodeposition and characterization of vertically aligned ZnO nanorod array film

Electrodeposition of ZnO Nanotube Arrays on TCO Glass Substrates

Single-Crystalline ZnO Nanotube Arrays on Conductive Glass Substrates by Selective Disolution of Electrodeposited ZnO Nanorods

Hydrothermally Grown ZnO Micro/Nanotube Arrays and Their Properties

Electrochemical/Chemical Synthesis of Highly-Oriented Single-Crystal Zno Nanotube Arrays on Transparent Conductive Substrates

Fabrication and characterization of single-crystalline ZnTe nanowire arrays

Substrate effect on Electrodeposition of ZnO nanorod Arrays

Selective Oxygen-Plasma-Etching Technique For The Formation Of Zno-Fto Heterostructure Nanotubes And Their Rectified Photocatalytic Properties

Synthesis of ZnO nanotube arrays and heterostructures of Cu-ZnO coaxial nanotubes by electrodeposition-oxidation method.

Low-temperature Synthesis and Photocatalytic Properties of ZnO Nanotubes by Thermal Oxidation of Zn Nanowires.

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

One-Step Hydrothermal Process for Self-Assembly of Zinc Oxide Nanorods Array on Al-Doped Zno Nanoplate Surface

Synthesis and Characterization of Cu2ZnSnSe4 Nanotube Arrays on Fluorine-Doped Tin Oxide Glass Substrates

Conversion Process of ZnO Nano-/Micro-Rods into Nano-/Micro-Tubes and Cathodoluminescence Characterization

Hydrothermal Growth and Characterization of ZnO Nanorods