Abstract:Abstract Most of the recent nanodevices are fabricated by using high-efficiency deposition methods and patterned via high-resolution lithography. However, there are drawbacks for the methods including small-scale product, high cost consumption, and multi-step processes. To reduce these disadvantages, this work focuses on the usage of sol-gel synthesis and spin coating method to fabricate ZnO seed layer onto glass substrates. All of substrates were patterned by conventional UV photolithography at exposure time of 7 seconds, then ZnO nanorods were hydrothermally grown at 90°C for 2, 3, and 4 hours, respectively. All of samples were characterised by scanning electron microscope (SEM) which revealed the sharp and smooth tip hexagonal structure at different hydrothermal time. The evolution of the nanorods’ growth was investigated, and the diameters were estimated. Moreover, crystal quality was revealed by x-ray diffractograms. It was clear that the domination of c-axis plane occurred for all the samples associates with the crystallinity of the nanostructures. This indicated escalating of the non-monodirectional growth plane in increasing nanorods’ diameter as the nanorods are polycrystal. Furthermore, the optical properties of the samples were observed by UV-visible spectroscopy and photoluminescence technique (PL). UV-visible spectroscopic data showed diminishing of the energy band gap when the diameter grew up. PL data revealed the reduction of the intensity ratio at near-band-edge peak versus oxygen vacancy peak. This information pointed to the decreasing trend of the crystal quality with escalating growth time.

Hydrothermal Growth and Characterization of ZnO Nanorods

Effect of UV irradiation on the properties of ZnO nanorod arrays prepared by hydrothermal method

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Influence of hydrothermal time on structural properties of ZnO nanorods grown on spin-coated ZnO seeding layer

Growth and Formation Mechanism of C-Oriented ZnO Nanorod Arrays Deposited on Glass

Ordered Growth and Photoluminescence of ZnO Nano-Arrays on Silicon Substrates with Seed Film by Hydrothermal Method

Low temperature growth and properties of ZnO nanorod arrays

Hydrothermal Synthesis and Optical Properties of ZnO Nanostructured Films Directly Grown From/on Zinc Substrates

Preparation and characterization of ZnO nanorods

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Hydrothermal self-assembling of ZnO nanorods into sphere-like superstructures and their optical characteristics

Preparation of microstructured ZnO nanorod photoelectrode

Effect of Temperature and Growth Time on Vertically Aligned ZnO Nanorods by Simplified Hydrothermal Technique for Photoelectrochemical Cells

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Fabriction of ZnO Nanorods with Strong UV Absorption and Different Hydrophobicity on Foamed Nickel under Different Hydrothermal Conditions

Hydrothermal Preparation of ZnO Nanorods Using Zinc Powder As Precursor and Their Characterization