New-featured Dry Desulphurization Analysis on the Magnesia-Base Adsorbent Flue Gas
Peng-jie LIU,Yu GAO,Xiao-min HU,Yun LI,Yang ZHANG,Ying LIU
DOI: https://doi.org/10.3969/j.issn.1009-6094.2008.03.008
2008-01-01
Applied Mechanics and Materials
Abstract:The present paper is concerned about our newly improved method in preparing magnesia-base adsorbent through our study of coprecipitation and flue gas-treated dry desulphurization. For this purpose,first of all,we have conducted experimental analogy by burning the coal flue gas desulphurization so as to analyze the desulfuration efficacy,its content of sulfur,the desulfuration time and the other similar factors by changing the adsorbent roasting time and temperature,as well as desulfuration process with or without oxygen presence. In doing so,we succeeded in granulating,roasting and drying the magnesium-based adsorbent and making it activated at different temperature ranges in 2 hours,so as to make the specific area of the adsorbent and sulfur capacity enhanced significantly. That is to say,it is possible to gradually increase the specific surface area lower than 550 ℃ so as to make it reach the maximum temperature of 550 ℃. Nevertheless,with further increase of temperature,the adsorbent specific area would begin to drop remarkably. At calcination temperature of 550 ℃,with the increase of baking time,the specific surface area and sulfur capacity tend to increase significantly and then reach their maximum value in 2h,and later would be slowly declining,with the fall tendency getting slower and slower in 3h. In addition,we have also found that,under three different conditions of the flue gas temperature,that is,30 ℃,90 ℃,150 ℃,the rise of the flue gas temperature is not favorable for the increase of desulphurization efficiency. Moreover,the simulated flue gas proves to be oxygen-absent,with the desulphurization efficiency dropping significantly,particularly within 3050min. Thus,our experimental results prove that oxygen is favorite for desulphurization,the adsorbent preparative roasting temperature should be at 550 ℃,at best roasting time length of 2 h. It also shows that it is possible to proceed flue gas dry desulphurization at the presence of magnesia base adsorbent with oxygen accelerating the process of desulphurization. What is more,it has proved that with the help of magnesia base adsorbent,the higher decomposition temperature,the more thorough decomposition reaction will be,and the more efficient the removing rate either of hydration water or of CO2,and,in turn,the easier the sinter,mechanical strength fall,as well as the quicker specific area degression and sulfur capacity homologization. From what is said above,it can be concluded that our analysis helps to disclose the essential process of desulphurization,which is by nature the production of SO2 with the help of oxygen and in which SO2 or SO3 are simultaneously united inside and outside of the superficial of magnesia absorbent's crystal plane. In addition,six steps prove to exist in the magnesium adsorbent gas-solid phase adsorption process.