Magnesia Absorbents of Dry Flue Gas Desulphurization

Peng-jie LIU,Yun LI,Xiao-min HU,Yu GAO,Yang ZHANG,Ying LIU

DOI: https://doi.org/10.3969/j.issn.1009-6094.2007.03.013

2007-01-01

Applied Mechanics and Materials

Abstract:This paper is inclined to present the authors' study results of the inexpensive magnesia sands from Dashiqiao area, Liaoning, to be applied as absorbents. As a piece of our research finding, it is found that the activation effect of the agent can be made greatly improved after 2 hours' calcinations at a temperature of 550 ℃. We have also worked out the optimum calcinations conditions through our experiments, with their surface turning to 21.398 2 m2/g from 12.225 6 m2/g, but their sulfur absorbing capacity being lowered after activation about 7.0 mg/g. In our experiments, the sulfur capacity of absorbents was enhanced by soaking Na2CO3 and NaCl with the absorbing capability being twice enhanced. That is to say, the sulfur capacity has been increased to 16.92 mg/g when Na2CO3 was added. In our experiments with desulphurization process and influential factors of desulphurization, we have found that the efficiency of desulphurization proves to be affected by such factors as oxygen content, steam content, and the coal smoke temperature. On the basis of the above experiments, technical conditions were also tested, whose results show that, when V(O2)∶V(SO2)=6-8, the coal smoke temperature would be 120150 ℃, V(H2O)∶V(SO2)=2-4, with SO2 concentration being 1 5003 000 mg/m3 and the layer thickness being 5-7 cm. At this moment, the desulphurization effect would have reached above 92%.