Simulation and Experimental Study on Pore Size Distribution of CaO from Limestone Calcination
XIA Ying-ying,FU Wei,HUANG Tao-hua,WANG Yi-fei,WANG Fu-chen
DOI: https://doi.org/10.3321/j.issn:1000-6761.2009.11.015
2009-01-01
Abstract:In order to find the relationship between the pore structure of CaO from limestone calcination and the desulfurization process,a mathematical model for describing the pore structure was developed,with which pore volume and specific surface area calculated.The calculated results agree well with that of actual measurements.With focus on following 4 pore size ranges: 0-5 nm,5-20 nm,20-100 nm and 100 nm above,3 samples respectively coded as A,B and C were analyzed.Results show that among the 3 samples tested,sample A,whose particle sizes are the largest,has the widest range of pore size distribution,the largest pore size corresponding to the peak value and the largest average pore radius;sample B,whose particle sizes are the medium,has the narrowest range of pore size distribution,the smallest pore size corresponding to the peak value and the smallest average pore radius;sample C,whose particle sizes are the smallest,may be partially sintered,and therefore resulting in larger pore radius corresponding to the peak value and larger average pore radius than sample B.Particles of sample B have the largest proportion of effective radius(5-20 nm) among the 3 samples,and therefore it is believed to have the best desulfurization effect.This assumption has been proved by actual experiments based on CaO with above 3 sizes.