Enhanced Interfacial Joining and Electrical Contact Performance of Eco-friendly Ag/Ti3AlC2 with Cu-Zn Contact Bridge via Induction Welding
Wanjie Sun,Kaige Zhang,Xinpeng Wei,Ximin Wu,Yundeng Zhang,Xuelian Wu,Lei Hu,Dandan Wang,Chunjun Cai,Yaping Wang,Peigen Zhang,ZhengMing Sun,Jianxiang Ding
DOI: https://doi.org/10.1007/s11665-024-09917-2
IF: 2.3
2024-08-19
Journal of Materials Engineering and Performance
Abstract:Eco-friendly Ag/MAX electrical contact materials have potentials in low-voltage switches for their ultra-high electrical/thermal conductivity and phase stability. However, the Ag/MAX electrical contacts confront common interfacial joining failures with contact bridge, leading to rapid degradation in electrical contact performance and operational lifespan. Herein, a simple and efficient induction welding technique assisted with the B45AgCuZn solder is applied to join the typical Ag/Ti 3 AlC 2 with the Cu-Zn contact bridge. The welding qualities of the joint Ag/Ti 3 AlC 2 /Cu-Zn under varying welding conditions (temperature, holding time) are checked based on the single-factor and orthogonal experiments by micro-morphology observation and ultrasonic C-scan. The electrical conductivity, mechanical strength, and cyclability of the Ag/Ti 3 AlC 2 /Cu-Zn are investigated. Moderate welding temperature and extended holding time are preferred to guarantee a well-joint interface without pores, cracks, and unwelded regions. Moreover, an enhanced mutual element diffusion resulting in the formation of a network-like AgCu alloy interphase further promotes the interfacial joining between Ag/Ti 3 AlC 2 and Cu-Zn contact bridge at the welding conditions of 580 °C/6 s. Consequently, the Ag/Ti 3 AlC 2 /Cu-Zn electrical contact demonstrates a brazing rate of 100%, high hardness (135.0 HV), and shear strength (86.7 MPa), low electrical joining resistance (0.053 mΩ), and long cycling stability (10000 times discharging), which is comparable to traditional Ag/CdO. These results lay a foundation for developing Ag/MAX electrical contact with ultra-high performance and ultra-long service life.
materials science, multidisciplinary