Abstract:The mechanical and rheological characterizations of flexible investment casting patterns capable of 3D printing are reported. The wax pattern was composed of microcrystalline hydrocarbon wax (DMW7478), Piccotex 75 (a copolymer of α–methyl–styrene and vinyl toluene with a 75/25 molar ratio, respectively) and Escorene (a copolymer of ethylene and vinyl acetate with a 72/28 mass ratio, respectively). It was found that in order to obtain a wax pattern with appreciable mechanical properties, the content of the microcrystalline hydrocarbon wax in these blends should not exceed 30% (m/m). Thus, a series of patterns with 28% (m/m) wax and varying Piccotex and Escorene contents spanning from 0 to 72% (m/m) was prepared. The dependence of the dynamic viscosities of the wax patterns on the composition was described using a stretched exponential model, whereas their variations with the temperature were interpreted in terms of the Arrhenius–Guzman equation. Furthermore, the slopes of the lines fitted to the viscosity versus temperature curves at the pour point decreased linearly with the Piccotex content. Non-Newtonian changes in the shear stress with the shear rate and shear stress crystallization were observed at temperatures near the pour points. The mechanical properties were evaluated using the uniaxial tensile mode and by three-point bending experiments. It was found that the stress (σ) versus the relative elongation (ε) curves can effectively be rendered by means of the standard linear solid (SLS) viscoelastic model. In addition, it was also established that the Young's modulus varied according to a sigmoid-type curve with the piccotex content, while the yield stress decreased linearly with the concentration of Piccotex. In addition, based on the spooling suitability and printability, the patterns were rated and it was found that the most appropriate wax pattern compositions for 3D printing were those which contained 30% (m/m) and 35% (m/m) Piccotex.

Cavity Pressure and Dimensional Accuracy Analysis of Wax Patterns for Investment Casting

The Influence of Injection Processing on the Shrinkage Variation and Dimensional Stability of Wax Pattern in Investment Casting

Numerical Simulation of the Wax Injection Process for Investment Casting

Simulation Study on Wax Injection for Investment Casting

The Propagation and Accumulation of Dimensional Shrinkage in Investment Casting

Dimensional Shrinkage Prediction Based on Displacement Field in Investment Casting

Simulation and Experimental Analysis on Non-circular Cross-section Parts Residual Wall Thickness of Water-assisted Injection Molding

The Propagation and Accumulation of Dimensional Shrinkage for Ring-to-ring Structure in Investment Casting

Experimental and Numerical Analysis on Core Deflection During Wax Injection

Experimental Study of Injection Conditions for A Thin-Walled Wax Pattern Using Response Surface Methodology

Effect on Residual Wall Thickness of Parts with Floating Core Injection of Water-Assisted Injection Molding

Influence of Complex Structure on the Shrinkage of Part in Investment Casting Process

Numerical Simulation and Intelligent Optimization of Wax Injection in Investment Casting

Effects of process parameters on dimensional precision and tensile strength of wax patterns for investment casting by selective laser sintering

Effect of Mold Material on Shrinkage of Investment Casting Wax Pattern

Numerical Simulation of Vacuum Investment Casting Cartridge Receiver

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Study on Numerical Simulation of Mold Filling and Solidification Processes under Pressure Conditions

Influences of Material Selection, Infill Ratio, and Layer Height in the 3D Printing Cavity Process on the Surface Roughness of Printed Patterns and Casted Products in Investment Casting

Flexible Investment Casting Wax Patterns for 3D-Printing: Their Rheological and Mechanical Characterizations

An investigation of ceramic shell thickness uniformity and its impact on precision in turbine blade investment casting