Abstract:Abstract In this study, an Ar/O 2 plasma mixture treatment with different proportions of O 2 was used to reduce the oxygen vacancy density in an amorphous indium gallium zinc oxide (a-IGZO) thin film. The objective was to enhance the field-effect carrier mobility in a thin-film transistor (TFT) with the IGZO film as the channel layer. Atomic force microscopy revealed that the roughness of the IGZO film after plasma treatment was higher than that of the untreated film; however, the surface roughness of the IGZO film decreased after the proportion of O 2 was increased in the plasma. The Hall measurement results showed that the resistivity of the plasma-treated IGZO film increased with a decrease in the electron concentration in the film; in addition, the carrier mobility considerably increased. The IGZO TFT fabricated from this film exhibited a high field-effect carrier mobility of 36 cm 2 V −1 s −1 , a subthreshold swing (SS) of 1.25 V/decade, an I OFF current of 4.58 × 10 −11 A, and an I ON / I OFF current ratio of 7.55 × 10 5 . To further improve the device performance, the plasma-treated IGZO films were subjected to thermal annealing with the annealing temperature ranging from 100 °C to 300 °C. After the annealing process, the plasma-treated IGZO TFTs demonstrated a further improvement in the device performance with a field-effect carrier mobility of 38.8 cm 2 V −1 s −1 , SS of 0.7 V/decade, I OFF current of 1.04 × 10 −11 A, and an I ON / I OFF current ratio of 9.93 × 10 6 . In addition, a reliability test was performed to evaluate the stability of the IGZO TFT devices, which revealed that the threshold voltage maintained a high degree of stability during the long-term tests. Therefore, the plasma-treated IGZO TFTs with subsequent postgrowth annealing could be helpful for the fabrication of next-generation flat-panel displays.

Influence of Plasma Treatment on Optical and Electrical Properties of A-Ingazno Films

Modulation of Optical and Electrical Properties of Sputtering-Derived Amorphous Ingazno Thin Films by Oxygen Partial Pressure

Study on the optical thin film deposited by plasma ion plating

Deposition and Characterization of AZO Thin Films on Flexible Glass Substrates Using DC Magnetron Sputtering Technique

Influence of Oxygen Plasma Treatment on the Amorphous IGZO Thin Film Transistors

Surface Pattern and Optical Properties of In-doped ZnO Thin Films by Hydrothermal Method

Investigation of oxygen plasma treatment on the device performance of solution-processed a-IGZO thin film transistors

Structural, Electrical, and Optical Properties of ZnInO Alloy Thin Films

Improvement of device characteristics of plasma-treated indium gallium zinc oxide thin-film transistors through thermal annealing

Investigation of the Microstructure, Optical and Electrical Properties of In-Ga-Zn Oxide Thin Film Using the Sol-Gel Method

Dependence of Electrical and Optical Properties of IGZO Films on Oxygen Flow

Effect of Oxygen Plasma Treatment on the Performance of GQDs-Modulated InGaZnO Thin-Film Transistors

Comparison of the electrical and optical properties of direct current and radio frequency sputtered amorphous indium gallium zinc oxide films

Optimizing Oxygen Plasma Treatment Time to Improve the Characteristics of a-IGZO Thin-Film Transistors and Resistive-Load Inverters

Optical and electrical properties of room temperature prepared α-IGZO thin films using an In2Ga2ZnO7 ceramic target

Effects of Oxygen Plasma Treatment on the Surface Properties of Ga-doped ZnO Thin Films

Effect of annealing on characteristics of amorphous InGaZnO thin film transistors fabricated by sol-gel technical

Effect of surface treated amorphous Si–Zn–Sn–O on the electrical properties of thin film transistors by Ar plasma treatment

Ultrasonic Treatment-Induced Enhancement of Mechanical and Electrical Properties in InGaZnO Thin-Film Transistors

Effect of PVD Process on the Crystallization of IGZO Thin Films

Influence of Low Temperature Plasma Treatment on Surface Insulation Performance of Polyimide Film