Abstract:CdS nanocrystals including nanorods and faceted nanoparticles were prepared via thermolysing cadmium ethylxanthate in hot hexadecylamine (HDA) solution. In order to control the shape and size of the nanocrystals, the influence of reaction conditions (such as reaction temperature, monomer (single-source precursor-cadmium ethylxanthate) concentration and reaction time, etc.) on the morphology, the surface states and the dispersivity of the CdS nanocrystals was comprehensively investigated. The CdS nanocrystals were characterized by means of transmission electron microscopy (TEM), X-ray diffraction (XRD), absorption spectroscopy and photoluminescence spectroscopy. It was found that under the conditions of high monomer concentration and adequate reaction time (3 h), long multi-armed nanorods were produced dominantly when the reaction temperature was not higher than 200degreesC, while at high temperature (260degreesC), the formation of short single-armed nanorods was preferred. When the monomer concentration was low and the reaction time was much longer (such as 12 h), spherical-shaped nanocrystals were mainly obtained, while if the reaction time was between 4-6 h, faceted nanocrystals were produced. The mechanism of the effect of the reaction conditions on the shape and size of the nanocrystals is discussed. The variation of reaction conditions can shift the reaction system between thermodynamic and kinetic control, which determines the morphology of the resultant nanoparticles. The formation of anisotropic rod-like CdS nanocrystals was found to be a highly kinetics-driven reaction, and a high monomer concentration in the reaction environment is a necessary condition for synthesizing rod-like CdS nanocrystals. By optimal combination of the reaction temperature, monomer concentration and reaction time, size- and aspect ratio-tunable one-dimensional (1D) CdS nanorods and hexagonal-like CdS nanocrystals which self-assembled into supperlattice arrays were obtained.

Surface-roughness-assisted formation of large-scale vertically aligned CdS nanorod arrays via solvothermal method

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

One-Step Fabrication of CdS Nanorod Arrays Via Solution Chemistry

Surfactant–ligand Co-Assisted Solvothermal Technique for the Synthesis of Different-Shaped CdS Nanorod-Based Materials

Large-scale fabrication of CdS nanorod arrays on transparent conductive substrates from aqueous solutions

Controlled Synthesis of Highly Orientation-Ordered Single Crystal Cd1−Zn S Nanorod Array

Synthesis of Brush-Like CdS Nanorod Arrays Through a Novel Hydrothermal Reaction of Simultaneous Solvent-Oxidation-hydrolysis

Synthesis of rod-, twinrod-, and tetrapod-shaped CdS nanocrystals using a highly oriented solvothermal recrystallization technique

Effect of Solvents on Morphology and Size of CdS Nanoparticles via a Solvothermal Route

INDEPENDENT GROWTH OF LARGE SCALE CdS NANOROD ARRAYS ON DIFFERENT INTERFACES WITH EFFICIENT PHOTOELECTRICAL PERFORMANCE

Double-dentate solvent-directed growth of multi-armed CdS nanorod-based semiconductors

A Facile Single-Source Route to CdS Nanorods.

Controlled synthesis of CdS nanorods and hexagonal nanocrystals

Formation Process of Cds Nanorods Via Solvothermal Route

Self-assembly of CdS: from nanoparticles to nanorods and arrayed nanorod bundles

Synthesis and Characteristics of Large-Area and High-Filling CdS Nanowire Arrays in AAO Template.

Synthesis and Formation Mechanisms of CdS Nanorods by Hydrothermal Method

Controlled growth of high-density CdS and CdSe nanorod arrays on selective facets of two-dimensional semiconductor nanoplates