Abstract:CdS nanorods of high aspect ratio were synthesized through the route of chemical bath deposition under a mild condition. Diphenylthiocarbazone (DPTA) was employed as an organic additive for the synthesis of CdS nanorods. The crystalline and microstructure of CdS nanorods were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns indicate the existence of both cubic and hexagonal phases in the samples. The sample with the pH value of 10.5 showed a hexagonal (111) peak of maximum intensity, indicating the preferential orientation along the c axis of hexagonal CdS phase. Meanwhile, the cubic phase appeared at the pH value of 10.5. The TEM images reveal that the morphology of CdS could be controlled by adjusting the pH value. Highly crystalline CdS nanorods with the diameter of about 50 nm and the length of about 3 mu m were obtained at the pH value of 10.5. The effects of the pH value on the formation of CdS nanorods were studied. The electrical properties of the samples were also investigated. The results show that the sample prepared with DPTA as the organic additive exhibited a much lower resistance than those prepared with PVA as the additive and in pure ethanol. There were two big pi bonds in a DPTA molecule, which benefited the electron transfer. Finally, the growth mechanism of CdS nanorods and electron transfer in DPTA modified CdS nanorods were discussed.

Synthesis and Characterization of Large-Scale Hierarchical Dendrites of Single-Crystal CdS

Biomolecule-Assisted Hydrothermal Synthesis Of Hierarchical Cds Dendrites

Biomolecule-Assisted Synthetic Route to Nanostructured Crystals: Synthesis of CdS Hierarchical Dendrites

Hydrothermal Synthesis, Characterization And Growth Mechanism Of Single Crystal Lead Titanate Pyrochlore Dendrites

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

HYDROTHERMAL SYNTHESIS OF DENDRITE-LIKE ZINC SULFIDE CRYSTALS

Synthesis Of 3-D Hierarchical Dendrites Of Lead Chalcogenides In Large Scale Via Microwave-Assistant Method

Novel hierarchical CdS crystals by an amino acid mediated hydrothermal process

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Large-Scale Synthesis of Single-Crystal Double-Fold Snowflake Cu2s Dendrites

Crystallization of Amorphous Colloids: an Effective Approach for the Rapid and Large-Scale Preparation of Antimony Sulfide Dendrites

Preparation and Growth Mechanism of CdS Nanorods via Chemical Bath Deposition

Hydrothermal Synthesis and Characterization of SrTiO3 Dendrites

Surfactant-Free Fabrication of Catio3 Butterfly-Like Dendrite Via A Simple One-Step Hydrothermal Route

Design and synthesis of novel single-crystalline hierarchical CdS nanostructures generated by thermal evaporation processes

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

Diphenylthiocarbazone (Dithizone)-Assisted Solvothermal Synthesis and Optical Properties of One-Dimensional Cds Nanostructures

Photochemical self-assembly synthesis and characterization of CdSe dendrites

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Self-assembly of CdS: from nanoparticles to nanorods and arrayed nanorod bundles