Influence of WO on the performance of a CrO –WO catalyst for the selective catalytic reduction of NO with NH3
Jingyi Feng,Qingshan Wang,Tong Wu,Shujie Gao,Kai Zhu,Dong Ye,Ruitang Guo
DOI: https://doi.org/10.1016/j.fuel.2024.130989
IF: 7.4
2024-05-01
Fuel
Abstract:A series of CrO x –WO x mixed-oxide catalysts was synthesized through the citric acid-assisted sol–gel method and used in the selective catalytic reduction of NO x with NH3 to eliminate NO x . The pristine CrO x displayed certain deNO x activity, achieving >90 % NO x conversion efficiency at the temperature range of 210 °C–230 °C. Its robust oxidative ability facilitated efficient activation of adsorbed NH3, contributing to relatively high low-temperature activity. However, at higher temperatures, the increased over-oxidation of NH3 led to additional NO x formation. Moreover, the comparatively weak acidity resulted in a lower NH3 coverage on the CrO x surface, causing a deficiency in reductant NH3 for NO x reduction and consequently a decrease in high-temperature activity. With WO x addition, the acidity of the catalysts was enhanced, which was primarily responsible for the high NH3 coverage on the catalysts’ surfaces. Furthermore, the reduction in the reactivity of Cr6+ and the number of chemisorbed oxygen species slowed NH3 activation and inhibited NH3 over-oxidation, shifting the catalyst’s operating temperature window toward higher ranges. At a fixed W/Cr molar ratio of 0.8, >90 % NO x was eliminated at the temperature range of 230 °C–390 °C. However, the relatively weak resistance of the CrO x –WO x mixed oxide to SO2 or Na, together with the irrecoverable deactivation upon long exposure to these two components, suggests the need for further modification to enhance the practicality of the catalyst.
energy & fuels,engineering, chemical