Abstract:The catalytic oxidation of CO over Cu-based catalysts has garnered significant interest due to their promising potential in addressing environmental pollution and enhancing industrial processes. Herein, we report a dual-stimuli strategy to boost the catalytic performance of CO oxidation via synergistically harnessing active Cu + species with oxygen vacancies by engineering the grain boundary of Cu–Mn catalysts. Nanorod-like MnO 2 with a tunnel structure was prepared by a hydrothermal method and employed as the catalyst support, where different amounts of Cu were further introduced via impregnation to obtain Cu/MnO 2 catalysts. It is found that apart from the highly dispersed Cu species within the MnO 2 lattice to create lattice mismatch and distortion, some Cu are present as oxidized nanoparticles over the MnO 2 surface, thus sparking off increased dislocations and grain boundaries. A combination of characterization methods demonstrates that the proportion of active Cu + species decreases with increasing amount of Cu, presenting an inverse relationship to the abundance of oxygen vacancies over the catalyst surface. Correspondingly, both Cu + species and oxygen vacancies are identified as the main active sites for the adsorption and activation of CO and O 2 , respectively. Therefore, a trade-off between the percentage of active Cu + species and oxygen vacancies for the 15% Cu/MnO 2 catalyst with a moderate Cu introduction contributes to its highest catalytic activity, with T 50 and T 90 reaching 66 °C and 89 °C, respectively. This investigation highlights the potential of synergistically harnessing active Cu + species with oxygen vacancies via grain boundary engineering for enhanced catalytic performance in CO oxidation applications.

Role of surface species in CO oxidation over CuO@LaMnO 3 nanocomposites: Effect of calcination temperature

CO Oxidation over Nanostructured Ceria Supported Bimetallic Cu–Mn Oxides Catalysts: Effect of Cu/Mn Ratio and Calcination Temperature

Effect of Calcination Temperature on Surface Oxygen Vacancies and Catalytic Performance Towards CO Oxidation of Co3O4 Nanoparticles Supported on SiO2

Enhancing the Low-Temperature CO Oxidation over CuO-Based -MnO<sub>2</sub> Nanowire Catalysts

Effect of Cu Doping on the Structure and Catalytic Activity of LaMnO_3 Catalyst

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation

Investigation on the Catalytic Combustion of CO over LaMn 1‐ X Cu X O 3 Promoted by Acid Treatment

Physicochemical and Catalytic Properties of La0.8K0.2CuxMn1-xO3 for Simultaneous Removal of NOx and Soot: Effect of Cu Substitution Amount and Calcination Temperature

Solid-State Construction of CuOx/Cu1.5Mn1.5O4 Nanocomposite with Abundant Surface CuOx Species and Oxygen Vacancies to Promote CO Oxidation Activity

Structure–activity Relationship of CuO/MnO2 Catalysts in CO Oxidation

Catalytic Performance of Manganese Doped CuO–CeO2 Catalysts for Selective Oxidation of CO in Hydrogen-Rich Gas

Engineering the grain boundary and surface sites of binary Cu–Mn catalysts to boost CO oxidation

Enhancing low-temperature CO removal in complex flue gases: A study on La and Cu doped Co3O4 catalysts under real-world combustion environment

Interfacial Cu+ promoted surface reactivity: Carbon monoxide oxidation reaction over polycrystalline copper–titania catalysts

Site‐Resolved Cu2O Catalysis in the Oxidation of CO

Low-Temperature Co Oxidation Over Cuo/Co3o4 Catalysts

Surface Properties and Catalytic Performance of La0.8K0.2CuxMn1–xO3 for Simultaneous Removal of NOx and Soot

Revealing the intrinsic nature of Cu- and Ce-doped Mn3O4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Facile synthesis of a CuMnO<sub><i>x</i></sub> catalyst based on a mechanochemical redox process for efficient and stable CO oxidation