Abstract:Reliable brazing of ZrO2 ceramic to TC4 alloy is crucial for the wide applications in aerospace industries and biomedical devices. However, the brazing mechanism of ZrO2 ceramic has not been investigated systemically compared to Al2O3 and Si3N4 ceramics. The nature of the reaction products adjacent to ZrO2 ceramic still remains somewhat elusive. In this study, ZrO2 ceramic and TC4 alloy was successfully brazed with inactive AgCu filler metal. The interfacial microstructure of the joints was characterized by scanning electron microscope (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The effect of brazing temperature on the microstructure and mechanical properties of the joints were investigated in details. The results revealed that Cu3Ti3O+TiO layers were formed adjacent to ZrO2 ceramic while Ti–Cu IMCs layers were formed at TC4 substrate. With increasing brazing temperature, the thickness of Cu3Ti3O+TiO layers and Ti–Cu IMCs layers increased obviously. The hardness and elastic modulus of reaction phases were characterized by nano-indentation to reveal the plastic deformability. The highest shear strength of 52.2MPa was achieved when brazed at 870°C for 10min.

Interfacial product of ZrB2-SiC brazing joint and growth kinetics of reaction layer

Interfacial Reaction and Growth Behavior of Reaction Layer of Si3n4/Si3n4 Joint Brazed by Cu-Zn-Ti Filler Alloy

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Interfacial Microstructure and Properties of In-situ TiB Reinforced ZrB2-SiC Joints

Microstructure and mechanical properties of ZrB2-SiC ceramic composite brazed joint

Interfacial Microstructure and Mechanical Properties of ZrB2SiC C Ceramic and GH99 Superalloy Joints Brazed with a Ti-modified FeCoNiCrCu High-Entropy Alloy

Interfacial reaction evolution of the ZrC ceramic joint diffusion bonded with Ni interlayer

Interfacial Reaction Behavior and Mechanical Characterization of ZrO2/TC4 Joint Brazed by Ag–Cu Filler Metal

Microstructures and Interfacial Behavior of Zirconia/stainless Steel Joint Prepared by Pressureless Active Brazing

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Microstructure and mechanical properties of ZrB2-SiC joints fabricated by a contact-reactive brazing technique with Ti and Ni interlayers

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Brazing of ZrB2–SiC–C and GH99 with AgCuTi/SiC Interpenetrating Network Structural Composite As an Interlayer

Effect of Zr addition on the interfacial reaction of the SiC joint brazed by Inconel 625 powder filler

Interfacial microstructure and reaction phases in Si3N4/Si3N4 joints brazed with Cu-Zn-Ti filler alloy

Interfacial Reaction and Brazing Behaviour of SiCf/SiC with Cf/C Composites Using Si-10Zr Alloy at High Temperatures

Microstructure and Mechanical Property of the Zrb2-Based Ultra-High-Temperature Ceramic Composites Brazed Joint

Microstructural evolution and growth behavior of in situ TiB whisker array in ZrB2- SiC/Ti6Al4V brazing joints

Interfacial Reaction of Brazing Joint of Alumina Ceramics to Mild Steel

Interfacial Microstructure and Mechanical Properties of TZM Alloy and ZrC Particle Reinforced Tungsten Composite Joint Brazed Using Ti-61Ni Filler