Abstract:Laser-induced damage of fused silica optics at 351 nm is a key factor limiting the output energy of high-power laser facility, especially the damage growth process. A comprehensive understanding of its damage growth behavior is of critical importance for high-power laser facility. Thus we study the laser-induced damage growth on the exit surface of fused silica under the subsequent illumination of 5 ns square pulses at 351 nm on a large-aperture high-power laser facility. Experiment is conducted with a 36 cm thick UV grade fused silica focus lens in clean atmosphere and at room temperature. 56 laser shots of 3 fluence in a range from 0.1 J/cm2 to 8.1 J/cm2 are fired during the experiment. And the damage initiation process and growth process are monitored and recorded with an online optics damage inspection instrument which has an optical resolution of about 50 m. Experimental results demonstrate that the sizes of exit-surface damage sites exponentially or linearly grow with laser shots and the damage growth rate increases with laser fluence. However, it is found that even under the same laser conditions the damage grow rate is not a fixed value, which means that besides the laser fluence other parameters also influence the damage grow process. In order to highlight some tendencies, we consider the single-shot damage growth rate and calculate the average of inside fluence bins. Statistical analysis shows that smaller sites tend to grow with larger growth rates than larger sites under the irradiation of the same laser fluence. This result indicates that damage growth rate is influenced by both laser fluence and damage site size. It suggests that the damage growth rule needs to be incorporated into a size-dependent growth effect. The result that higher growth rates are obtained for small damage sites may be related to the damage growth mechanism of fused silica. Damage crater of fused silica consists of a central core and numerous surrounding cracks. The defects in the central core absorb laser energy and yield plasma, then the plasma pressure will open the cracks on the periphery of the crater and lead to lateral and axial expansion of cracks which can be identified as damage growth. The fact that smaller sites grow faster than larger sites implies that smaller sites more efficiently couple laser energy into fracture energy. Our results have important implications for both the prediction of fused silica optics lifetime and the fundamental understanding of laser damage mechanism.

Laser damage growth characteristics of HfO2/SiO2 high reflection film at 1064 nm

Researches on Laser Damage Resistance of Optical Films

Laser-induced Damage Growth of Fused Silica at 351 Nm on a Large-Aperture High-Power Laser Facility

Laser-Induced Damage Growth on Larger-Aperture Fused Silica Optical Components at 351 Nm

Material ejection and layer peeling-off in HfO2/SiO2 thin-film beam splitters induced by 1ω and 3ω lasers

Laser-induced damage growth of large-aperture fused silica optics under high-fluence 351 nm laser irradiation

Investigating the material properties of HfO2/SiO2-based anti-reflection coatings during 1064 nm laser-induced breakdown in air and vacuum conditions

Numerical simulation on the damage behaviors of optical mirrors induced by film defects in high-power CW laser

Time-Dependent Resistance of Sol–Gel HfO2 Films to In Situ High-Temperature Laser Damage

Modulation of Microstructure and Optical Properties of Anti-Reflection HfO 2 Films by Sputtering Power and O 2 /ar Flow Ratio

Laser Damage Performance Study of Fundamental Frequency Dielectric Film Optical Elements

Behavior of 355 nm laser-induced damage growth in fused silica

Damage Behaviors of Silica Microparticles on Fused Silica Optics under 355 Nm High Fluence Laser

Effect of nanosecond laser pre-irradiation on the femtosecond laser-induced damage of Ta2O5/SiO2 high reflector

The Damage Property of Oxyfluoride Glasses Irradiated by a 351 Nm High Fluence Laser

Analysis and Experimental Investigation of Laser Induced Damage of Optics

Damage Morphologies of Al2O3 and Fe Particles Attached on the Input Surface of Fused Silica after Irradiation by a 355 Nm Laser.

Growth of Laser Initial Damage in Conditioned Fused Silica at 355 Nm

Dynamics of filamentary damage induced by nanosecond laser in fused silica

Fatigue Effect of Hafnia/silica High-Reflective Coatings under Multiple Laser Pulses at 1064 Nm

Effect of Polishing-Induced Subsurface Impurity Defects on Laser Damage Resistance of Fused Silica Optics and Their Removal with Hf Acid Etching