Abstract:This study compares the microstructure and tensile properties of Ti6Al4V components fabricated by laser direct metal deposition (LDMD) additive manufacturing (AM) in the transverse and longitudinal directions. The results show anisotropic tensile properties with the transverse direction having high tensile and fracture strengths and the longitudinal direction having a high elongation and reduction of cross section. The anisotropic mechanical properties are attributed to the anisotropic microstructural distribution. The transverse tensile specimen is composed of short columnar prior-β grains which grow perpendicular to the tensile direction, and have a lamellar structure. Along the β grain boundary, αGB and large α colonies were identified. However, the longitudinal specimen shows that the long β structure is parallel to the tensile axis and that the microstructure is composed of basket-woven α phases with shorter α plates and smaller colony sizes compared with those in the transverse specimen. The fracture mechanism induced by the anisotropic microstructure along the transverse and longitudinal directions was compared by examining the fracture process in real-time using uniaxial in-situ scanning electron microscopy (SEM) tensile testing. The results show that shear fracture, which is caused by the vertical β grain boundaries and large α colonies with long α plates, occurs in the transverse specimen. The shear mode is the main reason behind the enhanced tensile strength and fracture strength due to the high resistance to microcrack propagation. However, in the longitudinal specimens, symmetric necking behavior due to the fine α grains resulted in uniform deformation of the grains on both sides of the grain boundaries, inducing greater elongation.

Microstructure And Tensile Properties Of Laser Melting Deposited Ti-5al-5mo-5v-1cr-1fe Near Beta Titanium Alloy

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Selective laser melted near-beta titanium alloy Ti-5Al-5Mo-5V-1Cr-1Fe: Microstructure and mechanical properties

In-situ Investigation of the Anisotropic Mechanical Properties of Laser Direct Metal Deposition Ti6Al4V Alloy

Study of microstructure and compressive strength of a novel Ti-0.75Al-9.5V alloys manufactured by laser deposition melting

In-Situ Tensile Deformation Behavior Of As-Built Laser Direct Metal Deposited Ti-6al-4v Alloy At 200 Degrees C

Microstructure and mechanical properties of laser additive manufactured novel titanium alloy after heat treatment

Microstructure and Mechanical Property of Ti–5Al–5Mo–5V–3Cr–1Zr Alloy Fabricated by Selective Laser Melting with a Preheated Substrate

Microstructure and Mechanical Properties of Ti-6al-4v Components Fabricated by Laser Micro Cladding Deposition

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

Grain refinement and improved tensile properties of Ti5Al2Sn2Zr4Mo4Cr titanium alloy fabricated by laser solid forming

Study on the Relationship Between Microstructure and Mechanical Property in a Metastable Β Titanium Alloy

The Martensitic Transformation and Mechanical Properties of Ti6Al4V Prepared Via Selective Laser Melting

Solidification Microstructure and Mechanical Properties of Laser Additive Manufactured Near-α Ti-6Al-3Nb-2Zr-1Mo Titanium Alloy

Achieving Equiaxed Transition and Excellent Mechanical Properties in a Novel Near-β Titanium Alloy by Regulating the Volume Energy Density of Selective Laser Melting

Microstructure and Mechanical Properties of An Ultrahigh-strength Titanium alloy Ti-4.5Al-5Mo-5V-6Cr-1Nb Prepared Using Laser Directed Energy Deposition and Forging: A Comparative Study

Microstructural evolution and mechanical properties of Ti55531–0.5Nb fabricated by selective laser melting under different heat treatments

Micro-deformation behavior of laser melting deposited multi-gradient TC4/TC11 alloy under tension-tension cyclic loading

Forging–microstructure–tensile properties correlation in a new near β high-strength titanium alloy

Optimization of Processing Parameters and Microstructure Evolution of (TiB+La 2 O 3 )/Ti6Al4V Manufactured by Laser Melting Deposition

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy