Low-temperature Firing and Microwave Properties of TiO 2 Modified Li 2 ZnTi 3 O 8 Ceramics Doped with B 2 O 3

Ming He,Huaiwu Zhang

DOI: https://doi.org/10.1007/s10854-013-1247-6

2013-01-01

Journal of Materials Science Materials in Electronics

Abstract:The low-temperature firing and microwave properties TiO2 modified Li2ZnTi3O8 ceramics with B2O3 addition have been developed. B2O3 addition could reduce the sintering temperature of Li2ZnTi3O8 ceramics from 1,150 to 900 °C, which is attributed to the formation of liquid phases during the sintering process observed by SEM. The 1.5 wt% B2O3 doped Li2ZnTi3O8 ceramics sintered at 900 °C have ε r = 23.3, Q × f = 48,817 GHz, and resonant frequency τ f  = −15.35 × 10−6/°C. Further, due to the compensating effect of rutile TiO2 (τf  = 450 ppm/°C), the temperature coefficient of τf for with TiO2 was adjusted to near zero value. The 1.5 wt% B2O3 doped Li2ZnTi3O8 ceramics with 3 wt% TiO2 dielectrics sintered at 900 °C exhibited the optimal microwave properties: εr = 25.9, Q × f = 46,487 GHz, and τf = −0.35 ppm/°C.