Abstract:In this study, a hot isostatic pressing (HIP) manufactured SiC particles (SiC p ) reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite was fabricated through ball-milling, HIP, homogenization, hot extrusion, solution treatment, and aging treatment. The results showed the presence of an interfacial reaction layer, MgAl 2 O 4 , around the SiC p , which enhanced the bonding between the particles and the matrix. The aging treatment resulted in the formation of different aging precipitates, which were featured by GP zone for T4, GP zone + η' (metastable MgZn 2 ) + η (stable MgZn 2 ) for T6 and GP zone + η' (metastable MgZn 2 ) for T6I4. The composite samples of T4, T6, and T6I4 exhibited different mechanical properties. Specifically, the elastic modulus was measured as 102.9, 103.4, and 102.3 GPa, the yield strength was 685.3, 598.1, and 619.7 MPa, the ultimate tensile strength was 713.6, 618.9, and 633.3 MPa, and the elongation was 2.2%, 1.8%, and 2.8%, respectively. Furthermore, the corrosion behavior of the composite was evaluated through electrochemical, intergranular corrosion, and exfoliation corrosion. The corrosion current density was found to be 3.17 × 10 −7 , 4.97 × 10 −7 , and 3.67 × 10 −7 A cm −2 , the corrosion potential was measured as −0.70, −0.81, and −0.56 V, and the maximum intergranular corrosion depth was 139.9, 167.8, and 106.2 μm for T4, T6, and T6I4, respectively. The severity of exfoliation corrosion varied, with T4 showing severe pitting, T6 exhibiting moderate pitting, and T6I4 displaying slight pitting. The strengthening mechanism and load transfer strengthening of the composites were discussed in detail based on theoretical calculations, and the anti-corrosion mechanisms were also analyzed.

Structure of GP Zones in Al–Si Matrix Composites Solidified under High Pressure

EXPERIMENTAL STUDY ON THE PHASE RELATIONS OF THE SYSTEM Mg2SiO4-MgAl2O4 AT HIGH PRESSURE AND HIGH TEMPERATURE

Atomic structure of clusters and GP-zones in an Al-Mg-Si alloy

On the Guinier-Preston zones in selective laser melted AlSi10Mg alloy

High resolution electron microscopy on the layered structures of GP zones in an Al-1.7at%Cu alloy

Nano-Phase and SiC–Si Spherical Microstructure in SiC/Al-50Si Composites Solidified under High Pressure

Small-angle scattering from GP zones in Al-Cu alloy

GPB-II zone in Si microalloyed Al–Zn–Mg–Cu alloy and its strengthening effect

Interfacial Regulation and Fracture Mechanism of Al–Si/SiC Composites Infiltrated under Super-Gravity Field

In situ Transmission Electron Microscopy Investigation of Nucleation of GP Zones Under Natural Aging in Al-Zn-Mg Alloy

Study on Microstructural Evolution and GP Zone Strengthening Mechanism by Solution and Aging Treatment in Non-dendritic Mg-6Zn-5Al Magnesium Alloy

Influence of Super-Gravity Coefficient on Spatial Distribution of Solidification Structure in Al-14.5Si Alloys

Morphological evolution of GP zones and nanometer-sized precipitates in the AA2050 aluminium alloy

Interfacial Segregation and Precipitates Behavior in the Ultrafine Grained Al-based Metal Matrix Composites

Guinier-Preston zones observed by high-angle annular detector dark-field scanning transmission electron microscopy

Phase Characterization and Formation Behavior in 6 Wt% Si High-silicon Austenitic Stainless Steel During Isothermal Aging

Growth Mechanism of Eutectic Si in Super-Gravity Solidified Al-Si Alloy During Annealing

Experimental examination of strain field within GP zone in an Al–Zn–Mg–Cu alloy

Evolution of precipitates in Mg?7Gd?3Y?1Nd?1Zn?0.5Zr alloy with fine plate -like 14H-LPSO structures aged at 240?C

Microstructure and properties of a HIP manufactured SiC p reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite

The copper content of Guinier–Preston (GP1) zones in Al–1.84 at.% Cu alloy