Microstructure and tribological properties evolution of Ni-Mo-SrSO 4 composites as a function of Mo contents at different temperatures
Feng Liu,Xianfang Wang,Jingshu Ren,Weifeng Cao,Ruisheng Guo,Wenwen Zhao,Junhong Jia
DOI: https://doi.org/10.1016/j.jmrt.2023.05.188
IF: 6.267
2023-05-26
Journal of Materials Research and Technology
Abstract:Ni-Mo-SrSO 4 composites with different Mo amount were prepared by hot pressing in a vacuum. The oxygen-deficient environment derived from the degradation of SrSO 4 during fabrication process led to the formation of SrMoO 4 , Sr 2 NiMoO 6 , and SrO in the sintered composites. With the increment in the contents of Mo, excessive dissolved Mo atoms accelerated the oxidation of Ni in the oxygen-deficient environment, which eradicated SrMoO 4 phase. As compared to sintered material containing Sr 2 NiMoO 6 and SrO, the appearance of SrMoO 4 led to a distinct decrease in the density and microhardness. To reveal the effect of SrMoO 4 on the wear mechanism, the tribological properties of the sintered composites against Al 2 O 3 ball were investigated at room temperature (RT) and 800 °C. The result indicated that the in-situ composite consisting of 80.75 wt.% Ni, 14.25 wt.% Mo, and 5 wt.% SrSO 4 exhibited good friction and wear properties at RT and 800 °C, which was attributed to the development of the intact tribofilm with grooves consisting of SrMoO 4 , Sr 2 NiMoO 6 , NiO, and h-MoO 3 at RT and the synergistic lubricating effect of SrMoO 4 , Sr 2 NiMoO 6 , and oxides (NiO, α-MoO 3 , SrMoO 4 , α-NiMoO 4 , and β-NiMoO 4 ) at 800 °C.
materials science, multidisciplinary,metallurgy & metallurgical engineering