Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Effect of Temperature on the Friction and Wear Behavior of Electroless Ni–P–MoS2–CaF2 Self-Lubricating Composite Coatings

Effects of Temperature and Normal Load on Tribological Behavior of Nickel-Based High Temperature Self-Lubricating Wear-Resistant Composite Coating

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

High-Temperature Friction and Wear Behavior of Nickel-Alloy Matrix Composites with the Addition of Molybdate

Performance of MoS2/Zr Composite Coatings at Different Deposition Temperatures

Friction and wear behavior of Ni-P-carbon nanotubes (CNTs) electroless composite coating

Friction and Wear of Electroless Ni-P-CS Composite Coating

Friction and Wear Properties of Electroless Ni-P- (If-Mos2) Composite Coatings in Humid Air and Vacuum

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

High temperature tribological performance of nickel-based composite coatings by incorporating multiple oxides (TiO2–ZnO–MoO3)

High temperature tribological behaviors and wear mechanisms of NiAl-MoO3/CuO composite coatings

Effect of Temperature and Load on Tribological Behavior in Laser-Cladded FeCrSiNiCoC Coatings

High Temperature Tribology Behaviors of Brush Plated Ni–W–Co/SiC Composite Coating

Friction and Wear Behavior of Electroless Wear-Resistant and Self-Lubricating Ni-P Composite Coatings

Characterization and Wear Behaviors of Electrodeposited Ni-MoS2/SiC Composite Coating

Effect of temperature on the tribological properties of Polytetrafluoroethylene/Kevlar fabric/phenolic composites

Microstructures and Properties of Nanostructured TiN/MoS2/Ag Composite Film Prepared by Pulsed Laser Deposition

Microstructure and tribological properties evolution of Ni-Mo-SrSO 4 composites as a function of Mo contents at different temperatures

The influence of nano-CeO2 on tribological properties and microstructure evolution of Cr3C2-NiCrCoMo composite coatings at high temperature

A Comparative Study of Laser Cladding High Temperature Wear-Resistant Composite Coating with the Addition of Self-Lubricating WS2 and WS2/(Ni–P) Encapsulation