Abstract:Due to the randomness of hard and brittle material damage evolution, assessing damage and interpreting mechanisms is challenging. This study focuses on analyzing material damage mechanisms by employing extensive multi-source heterogeneous data to extract quantitative information. A machine vision-based method for detecting and assessing defects in ceramics was proposed, achieving 98 % accuracy. Leveraging this method in scratching experiments, the progression of damage and micro-failure mechanisms in Si3N4 was investigated through the analysis of defect area distribution, force and acoustical signals. Results revealed that the distribution of defect areas conforms to a three-parameter Weibull distribution. At scratch depths of 0.01, 0.02 mm, approximately 90 % of damage accumulated within 1e2–1e4 μm 2 ; conversely, 0.03–0.06 mm led to a decrease to 30 – 40 %. Extensive crack propagation occurs within 0.02–0.03 mm, resulting in the intersecting formation of spalling blocks. Damage evolution occurs in three stages: shallow and small cracks with scattered spalling blocks in the first stage, deep and long cracks with continuous and irregularly shaped spalling blocks in the second stage, and nearly no cracks with continuous and regularly shaped blocks in the third stage. This study not only proposes an efficient method to detect and evaluate ceramic defects, but also deeply understands the evolution process of material damage mechanism. Considering defect distribution and statistical trends, this research not only provide guidance for the optimization of machining parameters, especially in the scene of specific precision and high removal rate. At the same time, the damage evolution and failure mechanism of Si 3 N 4 provide useful experimental basis and data support for deepening the understanding of material behavior during ultra-precision grinding.

Characterization and Tensile Evaluation of Ceramics under Plate-impact Conditions

Evaluation and Measurement of Surface/Subsurface Crack Damage of Ground Ceramics

Method of Damage Characterization of Engineering Ceramics Grinding Surface

The Dynamic Response of Brittle Materials under Impact Loading

Quantification of micro-damage evolution process in ceramics through extensive analysis of multi-source heterogeneous data

Research on dynamic mechanical properties and damage model of ceramic materials under multi‐axial stress

Damage mode effects on fracture strength of ultra-high temperature ceramics

Contact Damage and Damage Tolerance of Dental Ceramics

Numerical Analysis of Thermal Shock Cracking Behaviors of Ceramics Based on the Force-Heat Equivalence Energy Density Principle

Size-dependent Damage and Fracture of Two-Layer Systems

Damage Evolution and Fracture of Ceramic Coating Systems in Circle Plate Bending Tests: Experimental Observation and Modeling

An elastic-plastic cohesive zone model for metal-ceramic interfaces at finite deformations

Strength evaluation of brittle ceramics with surface defects subjected to thermal shock

Experiment and Numerical Simulation of Damage Progression in Transparent Sandwich Structure under Impact Load

Investigation of Micro-defects in Dental Ceramics and Damage Evolution

A Shockless Plate-Impact Spalling Technique, Based on Wavy-Machined Flyer-Plates, to Evaluate the Strain-Rate Sensitivity of Ceramic Tensile Strength

Determination of the influence of particle spatial distribution and interface heterogeneity on tensile fracture of ordinary refractory ceramics by applying discrete element modelling

Numerical modeling of dynamic response and microcracking in shock-loaded polycrystalline transparent ceramic

Strength damage behavior analysis of silicon carbide(SiC) ceramic cylindrical shells under hydrostatic pressure based on the state-based peridynamics

Analysis, Simulation and Experimental Study of the Tensile Stress Calibration of Ceramic Cylindrical Pressure Housings

Coupled crystal plasticity and micromechanics damage model based on viscoplastic self-consistent theory and X-ray computed tomography