Abstract:The constitutive relation of micro-cracked ultra-high temperature ceramics deduced by energy method and the temperature-dependent critical energy release rate of ceramics were demonstrated in this paper. Taking advantage of the constitutive relation and temperature-dependent critical energy release rate, the thermal shock behavior of Al2O3 had been simulated firstly with finite element method. Results showed that the crack patterns of simulation approximated in the experiments. That confirmed the accuracy of our model. The ZrB2-based ceramic was then used as an example to study the effects of the temperature dependence of crack propagation criterion on the evaluation of thermal shock resistance of ultra-high temperature ceramics. In addition, given that the cracks forming during thermal shock lead to discontinuities in the ceramic material and influence thermal conduction. The interaction between thermal shock cracks evolution and thermal conduction, and the corresponding effects on the thermal shock behavior of ultra-high temperature ceramics were studied for the first time. Results indicated that the thermal shock crack patterns and temperature fields were significantly different while the thermal conductivities at the cracks were different for identical thermal shock conditions. Therefore, in order to improve the accuracy of simulation and the evaluation of thermal shock resistance of ultra-high temperature ceramics, the temperature dependence of the crack propagation criterion and the interaction between the cracks evolution and thermal conduction must be taken into consideration.

Strength evaluation of brittle ceramics with surface defects subjected to thermal shock

THERMAL SHOCK RESISTANCE ANALYSIS OF CERAMIC PLATE WITH SEMI-ELLIPTICAL SURFACE DEFECT

Thermal Shock Resistance of Brittle Ceramic Materials with Embedded Elliptical Cracks

Evaluation and Measurement of Surface/Subsurface Crack Damage of Ground Ceramics

Numerical Analysis of Thermal Shock Cracking Behaviors of Ceramics Based on the Force-Heat Equivalence Energy Density Principle

Thermal Shock of Semi-Infinite Cellular Ceramics

Modeling of Thermal Shock Spalling Crack in a Ceramic Slabs

Residual Strength of a Low‐Strength Ceramic with a Precrack Induced by Thermal Shock

One Dimensional Transient Thermoelastic and Associated Fracture Analysis of Long Porous Ceramic Plate

Failure process analysis of ceramic materials subjected to thermal shock

Mechanism Analysis of Thermal Shock Properties for Zrb2-20%Sicp-10%Aln Ultra-High Temperature Ceramic with the Surface Defects

Fracture Behavior and Thermal Shock Resistance Analysis of Thermoelectric Material Plates and Shells under Thermal and Electric Shocks

Fractal characterization of ceramic crack patterns after thermal shocks

Thermal Shock Properties of Ceramics

A Model for Determining Strength for Embedded Elliptical Crack in Ultra-high-temperature Ceramics

The Influential Factors Analysis of Surface Crack Propagation Behavior of ZrB2-20%SiC-10%AlN Ceramic Subjected to Thermal Shock

Simulation of the thermal shock behavior of ultra-high temperature ceramics with the consideration of temperature-dependent crack propagation criterion and interaction between thermal shock cracks evolution and thermal conduction

Thermal shock resistance analysis methodology of ceramic coating/metal substrate systems

Thermal Shock Resistance Analysis of a Semi-Infinite Ceramic Foam

Improving the Thermal Shock Resistance of Ceramics by Crack Arrest Blocks

Phase Field Modeling of Crack Propagation in Three-Dimensional Quasi-Brittle Materials under Thermal Shock