Abstract:TiAl-based alloy have potential as high temperature structural materials for aerospace applications, especially for thermal protection systems in aerospace vehicles including skin materials. Unfortunately, the ductility and formability of TiAl-based alloys are rather poor and thus gamma-TiAl sheets or foils are quite difficult to be manufactured by traditional methods and still far from practical applications. In the present work, commercial pure Ti foils and in-house fabricated TiB2/Al composite foils were alternately stacked and rolled to prepare Ti-(TiB2/Al) laminates, and then heat treatment was utilized to make liquid Al react with solid Ti, and finally TiAl-based composite sheet with multi-layer distributed reinforcement TiB2 particles were achieved. This method avoided the direct deformation of brittle TiAl billets and thus the near-net-shape processing of TiAl-based alloys sheets was feasible. Phase transformation and microstructure evolution during heat treatment were investigated and mechanical properties of the resulting micro-laminated TiB2-TiAl composite sheets were evaluated. The results showed that porous TiAl3 layers were produced by the reaction between liquid Al and solid Ti because of Kirkendall effect, and the following densification treatment under 50 MPa at 1300 degrees C for 2 h significantly improved the relative density of material. Subsequently, the reaction diffusion between TiAl3 and residual Ti proceeded in the following heat treatment, and finally fully lamellar (alpha(2)-Ti3Al+gamma-TiAl) layers were obtained. TiB2 particles did not participate in any reaction and remained, and displayed multi layered distribution in the matrix (alpha(2)-Ti3Al+gamma-TiAl) layers. TiB2 rich layer hindered the coarsening of lamellar colony of (alpha(2)-Ti3Al+gamma-TiAl) layer. Tensile properties at 800 degrees C of multi layered TiB2 TiAl composite sheets remarkably increased because of an increase of energy dissipation caused by plastic deformation.

Preparation of Multi Layered Ti-Al Alloys by Solid Reaction

Growth Kinetics of TiAl3 Layer in Multi-Laminated Ti–(TiB2/Al) Composite Sheets During Annealing Treatment

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

Reaction behaviors occurring in Ti/Al foil metallurgy

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Investigation on the Microstructure Homogenization in A Tial Based Alloy Prepared by Elemental Powder Metallurgy

Fabrication Of Multilayers Coatings Of Intermetallic Compound On Micro-Crystallization Ti-6al-4v Sheet By Al-Foil Pack Aluminizing

TiAl-BASED COMPOSITE SHEET WITH MULTI-LAYER DISTRIBUTED REINFORCEMENT PREPARED BY SOLID-LIQUID REACTION

Preparation Of Ti/Al/Al-Cf Multilayer Layered Composites And Its Interfacial Reaction

Application and microstructure control of TiAl intermetallics

Orderly Nucleation and Competitive Growth Behaviors of Ti-Al Intermetallic Compounds in Ti/TiAl3 Diffusion Couple under High Temperature

Investigation on a Fabrication Technique of TiAl Sheet

The Formation of Ti 3 Alp / Ti-6 Al-4 V Surface Layer Via Additive Friction Stir Processing Method

Synthesis of Tial Based Alloy by Mechanical Milling, Warm Pressing and Reactive Sintering

First Phase Selection in Solid Ti/Al Diffusion Couple

Layered Structure of Ni-Al Multi-Layered Metal-Intermetallic Composites Fabricated by In-Situ Reactions

Aluminothermal Reaction to Prepare Al-Ti-C Master Alloy

Characterization on Solid Phase Diffusion Reaction Behavior and Diffusion Reaction Kinetic of Ti/Al

Diffusion, Intrusion and Reaction Between Al-Containing Intermetallics and TiC Sintered Body During Thermal Pressure Holding

Micro-/nano-scale structure and elemental diffusion in the Al/Ti/Al sandwich structure