Abstract:TiAl alloy is one of the most attractive candidates for a new generation of high-temperature structural materials and has broad application prospects in the aerospace field. As a typical intermetallic material, TiAl is inevitably difficult to process using conventional methods. Election beam selective melting (EBSM) is an effective method of addictive manufacturing to prepare TiAl alloy with a complex structure. However, the microstructure of TiAl alloy formed using EBSM often contains defects such as pores, which seriously reduces the mechanical properties of the material. In this work, the effects of EBSM and post-processing procedures on the microstructure and mechanical properties of Ti-48Al-2Cr-2Nb alloy were studied. The results show that the microstructure of Ti-48Al-2Cr-2Nb alloy formed using the EBSM process was dense and composed of equiaxed γ-phase and double-phase regions. A large number of dislocations that formed due to thermal stress were clearly observed inside the Ti-48Al-2Cr-2Nb alloy. When the EBSM process parameters were 13.5 mA, 4.0 m/s, and 40.50 J/mm3, as the current intensity increased, the Al content decreased, the content of α2 phase increased, and the microstructure of the material was coarse. The results of the tensile test fracture morphology indicate that the Ti-48Al-2Cr-2Nb alloy exhibited brittle fracture during tensile deformation, lacking the typical yield deformation of metal materials. As the energy density of the EBSM process increased, the mechanical properties of the Ti-48Al-2Cr-2Nb alloy first increased and then decreased. The samples prepared with an energy density of 34.50~40.50 J/mm3 had excellent mechanical properties, of which the maximum tensile strength and maximum elongation reached 643 MPa and 2.09%, respectively. The phase composition of the Ti-48Al-2Cr-2Nb alloy after hot isostatic pressing (HIP) treatment remained unchanged from the EBSM samples, but there was a slight difference in content. There was an increase in the amount of γ phase and a decrease in B2 phase, accompanied by the generation of a massive γ phase after HIP treatment. Moreover, the number of dislocations inside the material increased. The Ti-48Al-2Cr-2Nb alloy after HIP treatment exhibited obvious plastic deformation characteristics, with a tensile strength of 679 MPa and elongation of 2.5%. A heat treatment of 900 °C/5 h was performed on the Ti-48Al-2Cr-2Nb alloy after HIP. The dislocation density of the Ti-48Al-2Cr-2Nb alloy decreased, and the B2 phase transformed from massive to lamellar.

TiAl-BASED COMPOSITE SHEET WITH MULTI-LAYER DISTRIBUTED REINFORCEMENT PREPARED BY SOLID-LIQUID REACTION

PREPARATION AND PROPERTIES OF TiB2/TiAl COMPOSITE SHEETS WITH LAYERED STRUCTURE

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Growth Kinetics of TiAl3 Layer in Multi-Laminated Ti–(TiB2/Al) Composite Sheets During Annealing Treatment

High Temperature Tensile Properties of in Situ TiBw/Ti6Al4V Composites with a Novel Network Reinforcement Architecture

Balancing the strength and ductility of Ti2AlC/TiAl composite with a bioinspired micro-nano laminated architecture

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

Strengthening and toughening of laminated TiAl composite sheets by titanium alloy layers and carbide particles

Enhanced high temperature mechanical properties and heat resistance of an Al–Cu–Mg–Fe–Ni matrix composite reinforced with in-situ TiB2 particles

Effect of TiB2 particles on thermal deformation behavior and mechanical properties of aluminum alloy

Fabrication of Al/Al-TiB 2 laminate composites via hot press sintering process: An insight into the mechanical properties and fracture behavior

Microstructure and Mechanical Properties of Ti-Al-Ti-Ti2AlNb Laminated Composites Based on the Ductile-brittle Structure

Enhancing strength-ductility synergy in nano-sized TiB 2 /Al composite via rapid solidification and thermo-mechanical processing

Enhanced mechanical properties of a novel heat resistant Al-based composite reinforced by the combination of nano-aluminides and submicron TiN particles

TiAl Alloy Fabricated Using Election Beam Selective Melting: Process, Microstructure, and Tensile Performance

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw

Study on microstructure and properties of TiBw/Ti-V-Al light weight high temperature shape memory composite

In-situ synthesized a dual-scale Ti 2 AlC reinforced TiAl composites with superior mechanical properties

Strengthening and toughening mechanisms of tailored Al/Al-TiB 2 laminated composites fabricated by hot press sintering process

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

A bicomponent TiAl alloy with superior compressive strength-ductility synergy prepared by powder metallurgy