Abstract:TiAl alloy is one of the most attractive candidates for a new generation of high-temperature structural materials and has broad application prospects in the aerospace field. As a typical intermetallic material, TiAl is inevitably difficult to process using conventional methods. Election beam selective melting (EBSM) is an effective method of addictive manufacturing to prepare TiAl alloy with a complex structure. However, the microstructure of TiAl alloy formed using EBSM often contains defects such as pores, which seriously reduces the mechanical properties of the material. In this work, the effects of EBSM and post-processing procedures on the microstructure and mechanical properties of Ti-48Al-2Cr-2Nb alloy were studied. The results show that the microstructure of Ti-48Al-2Cr-2Nb alloy formed using the EBSM process was dense and composed of equiaxed γ-phase and double-phase regions. A large number of dislocations that formed due to thermal stress were clearly observed inside the Ti-48Al-2Cr-2Nb alloy. When the EBSM process parameters were 13.5 mA, 4.0 m/s, and 40.50 J/mm3, as the current intensity increased, the Al content decreased, the content of α2 phase increased, and the microstructure of the material was coarse. The results of the tensile test fracture morphology indicate that the Ti-48Al-2Cr-2Nb alloy exhibited brittle fracture during tensile deformation, lacking the typical yield deformation of metal materials. As the energy density of the EBSM process increased, the mechanical properties of the Ti-48Al-2Cr-2Nb alloy first increased and then decreased. The samples prepared with an energy density of 34.50~40.50 J/mm3 had excellent mechanical properties, of which the maximum tensile strength and maximum elongation reached 643 MPa and 2.09%, respectively. The phase composition of the Ti-48Al-2Cr-2Nb alloy after hot isostatic pressing (HIP) treatment remained unchanged from the EBSM samples, but there was a slight difference in content. There was an increase in the amount of γ phase and a decrease in B2 phase, accompanied by the generation of a massive γ phase after HIP treatment. Moreover, the number of dislocations inside the material increased. The Ti-48Al-2Cr-2Nb alloy after HIP treatment exhibited obvious plastic deformation characteristics, with a tensile strength of 679 MPa and elongation of 2.5%. A heat treatment of 900 °C/5 h was performed on the Ti-48Al-2Cr-2Nb alloy after HIP. The dislocation density of the Ti-48Al-2Cr-2Nb alloy decreased, and the B2 phase transformed from massive to lamellar.

Fabrication Of Multilayers Coatings Of Intermetallic Compound On Micro-Crystallization Ti-6al-4v Sheet By Al-Foil Pack Aluminizing

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

HVAF deposition mechanism of γ-TiAl-based coating containing β phase

Structure and Properties of Ti-Al Intermetallic Coatings Reinforced with an Aluminum Oxide Filler

Surface Modification and Alloying of Aluminum and Titanium Alloys with Low-Energy, High-Current Electron Beams

TiAl Alloy Fabricated Using Election Beam Selective Melting: Process, Microstructure, and Tensile Performance

Fabrication of Ti3Al-Based Intermetallic Alloy by Laser Powder Bed Fusion Using a Powder Mixture

Microstructures and Phases in Electron Beam Additively Manufactured Ti-Al-Mo-Zr-V/CuAl9Mn2 Alloy

A novel approach to coating for improving the comprehensive high-temperature service performance of TiAl alloys

Achieving three-layered Al/Mg/Al sheet via combining porthole die co-extrusion and hot forging

Reaction behaviors occurring in Ti/Al foil metallurgy

Microstructures Of Components Synthesized Via Electron Beam Selective Melting Using Blended Pre-Alloyed Powders Of Ti6al4v And Ti45al7nb

Formation of a bimetallic Ti–Al material by a wire-feed electron-beam additive manufacturing

Microstructure characterization of AlCoCrFeNiTi high-entropy alloy coating produced by atmospheric plasma spraying

Interdiffusion mechanism at the interface between TiAl alloy and NiCoCrAlY bond coating

Orderly Nucleation and Competitive Growth Behaviors of Ti-Al Intermetallic Compounds in Ti/TiAl3 Diffusion Couple under High Temperature

Processing of Ti-24 Al-14 Nb-3 V alloy foils

Microstructure Formation and Mechanical Properties of Metastable Titanium-Based Gradient Coating Fabricated via Intense Pulse Ion Beam Melt Mixing

Hierarchical microstructure of a titanium alloy fabricated by electron beam selective melting

Microstructure, Microhardness, Fracture Toughness, and Abrasive Wear of In-Situ Synthesized TiC/Ti-Al Composite Coatings by Cold Spraying Combined with Heat Treatment

Microstructure evolution and tensile property of TiAl alloy using continuous direct energy deposition technique