Abstract:Highly ordered hexagonal mesoporous aluminosilicates (MAS-5) with uniform pore sizes have been successfully synthesized from assembly of preformed aluminosilcate precursors with cetyltrimethylammonium bromide (CTAB) surfactant. The aluminosilicate precursors were obtained by heating, at 100-140 degreesC for 2-10 h. aluminasilica gels at the Al2O3/SiO2/TEAOH/H2O molar ratios of 1.0/7.0-350/10.0-33.0/500-2000. Mesoporous MAS-5 shows extraordinary stability both in boiling water (over 300 h) and in steam (800 degreesC for 2 h). Temperature-programmed desorption of ammonia shows that the acidic strength of MAS-5 is much higher than that of MCM-41 and is comparable to that of microporous Beta zeolite. In catalytic cracking of 1,3,5-triisopropylbenzene and alkylation of isobutane with butene. MAS-5 exhibits greater catalytic activity and selectivity, as compared with MCM-41 and HZSM-5. The MAS-5 samples were characterized with infrared, UV-Raman, and NMR spectroscopy and numerous other techniques. The results suggest that MAS-5 consists of both mesopores and micropores and that the pore walls of MAS-5 contain primary and secondary structural building units, similar to those of microporous zeolites. Such unique structural features might be responsible for the observed strong acidity and high thermal stability of the mesoporous aluminosilicates with well-ordered hexagonal symmetry.

Highly hydrothermally stable Al-MCM-41 with accessible void defects

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Preparation of MCM-41 with high thermal stability and complementary textural porosity

Study on the hydrothermal stability of MCM-41 via secondary restructure

New Mineralization Agents for the Synthesis of MCM-41

Novel route in the synthesis of MCM-41 containing framework aluminum and its characterization

Comparison of disordered mesoporous aluminosilicates with highly ordered Al-MCM-41 on stability, acidity and catalytic activity

Thermal Stability of Structural Aluminum in the Mesoporous Molecular Sieve MCM-41

Synthesis and Characterization of AlMCM-41 Molecular Sieves

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Understanding of the High Hydrothermal Stability of the Mesoporous Materials Prepared by the Assembly of Triblock Copolymer with Preformed Zeolite Precursors in Acidic Media

Effect Of Structural Aluminum On The Mesoporous Structure Of Mcm-41

Influence of cations (Li+, Na+, K+)for synthesis mesoporous molecular sieve MCM-41 and their properties

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Synthesis of Mesoporous Molecular Sieve Al-MCM-41 in Ammonia Water and Its Characterization

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

A TIME DEPENDENT STUDY FOR THE FORMATION OF ULTRASMALL Cs-AlMCM-41 HOLLOW NANOSPHERES

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Surface Properties of Al-Functionalized Mesoporous MCM-41 and the Melting Behavior of Water in Al-MCM-41 Nanopores

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors