Investigation of the Microporous Structure and Non-Framework Aluminum Distribution in Dealuminated Nanosized HZSM-5 Zeolite by 129xe NMR Spectroscopy
WP Zhang,XW Han,XC Liu,H Lei,XM Liu,XH Bao
DOI: https://doi.org/10.1016/s1387-1811(02)00335-9
IF: 5.876
2002-01-01
Microporous and Mesoporous Materials
Abstract:Variations in the microporous structure and non-framework aluminum (AlNF) distribution of HZSM-5 zeolite with a crystal size less than 100 nm dealuminated by thermal and hydrothermal treatment have been investigated by xenon adsorption and 129Xe NMR spectroscopy. The secondary pores in the nanosized HZSM-5 zeolite are observed directly via 129Xe NMR spectroscopy. As evidenced by 129Xe NMR and XPS, for the calcined microsized HZSM-5, most of the AlNF may deposit on its external surface, a small amount of AlNF may be located in its channels. However, for the calcined nanosized HZSM-5, most of the AlNF may be located in the channels, while a small amount of AlNF may be located on the external surface. After hydrothermal treatment at lower temperature, the distribution of AlNF in dealuminated nanosized HZSM-5 is heterogeneous. It is not only present in the channels and on the external surface as in the case of microsized HZSM-5, but also near the pore entrances at the outer edge of the crystallites. However, at higher steaming temperatures, more AlNF in both the microsized and the nanosized HZSM-5 zeolites will migrate to their external surface.