Abstract:Using tetraethylorthosilicate (TEOS), polymethylhydrosiloxane (PMHS) and aluminium isopropoxide (AIP) as the reactants, through a one-step nonsurfactant route based on PMHS–TEOS–AIP co-polycondensation, hydrothermally stable mesoporous aluminosilicates with different Si/Al molar ratios were successfully prepared. All samples exclusively showed narrow pore size distribution centered at 3.6nm. To assess the hydrothermal stability, samples were subjected to 100°C distilled water for 300h. The boiled mesoporous aluminosilicates have nearly the same N2 adsorption–desorption isotherms and the same pore size distributions as those newly synthesized ones, indicating excellent hydrothermal stability. The 29Si MAS NMR spectra confirmed that PMHS and TEOS have jointly condensed and CH3 groups have been introduced into the materials. The 27Al MAS NMR spectra indicated that Al atoms have been incorporated in the mesopore frameworks. The NH3 temperature-programmed desorption showed strong acidity. Due to the existence of large amount of CH3 groups, the mesoporous aluminosilicates obtained good hydrophobicity. Owing to the relatively large pore and the strong acidity provided by the uniform four-coordinated Al atoms, the excellent catalytic performance for 1,3,5-triisopropylbenzene cracking was acquired easily. The materials may be a profitable complement for the synthesis of solid acid catalysts.

Comparison of disordered mesoporous aluminosilicates with highly ordered Al-MCM-41 on stability, acidity and catalytic activity

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Comparative Study on the Structural, Acidic and Catalytic Properties of Nano-Sized and Large-Particulate Mesoporous Aluminosilicates

Synthesis, characterization, and catalytic properties of stable mesoporous molecular sieve MCM-41 prepared from zeolite mordenite

Hydrothermal synthesis and pore characterization of AlMCM-41

Synthesis and Catalytic Performances of Mesoporous Aluminosilicates of Cubic and Hexagonal Structure with Stronger Acid Sites

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Highly hydrothermally stable Al-MCM-41 with accessible void defects

Synthesis of Mesoporous Aluminosilicates with Enhanced Acidity from Preformed Beta Zeolite

STUDY ON ACID PROPERTIES OF MCM-41 MESOPOROUS MOLECULAR SIEVE MATERIALS

Novel synthesis of ordered mesoporous materials Al-MCM-41 from bentonite

Comparative study on the acidic and catalytic properties of AlMSU-2- and AlMCM-41-like samples: both synthesized from the same zeolite-like precursor

Synthesis and characterization of ionic liquid-functionalized alumino-silicate MCM-41 hybrid mesoporous materials

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Synthesis of hydrothermally stable, hierarchically mesoporous aluminosilicate Al-SBA-1 and their catalytic properties

Mesoporous Material Al-MCM-41 from Natural Halloysite

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Synthesis of Cubic Mesoporous Aluminosilicates with Enhanced Acidity

Hydrothermal Synthesis and Pore Characterization of AIMCM-41