Abstract:series of aluminophosphate-based tubular mesoporous molecular sieves without (UHM-1) and with substituted silicon (UHM-3) have been synthesized at room temperature in the presence of a cationic surfactant cetyltrimethylammonium chloride (CTACl) and an organic base tetramethylammonium hydroxide (TMAOH). Characterization by powder X-ray diffraction (XRD), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), N-2 adsorption, and Al-27, P-31, and Si-29 magic-angle-spinning (MAS) NMR spectroscopies has been carried out to understand both the pore structures and the local atomic arrangements of these solid products. The synthesis of UHM-1 and UHM-3 is successful only at room temperature within the following molar gel composition: Al2O3:(0.6-3.4) P2O5:(0.0-1.0) SiO2:(0.24-0.50) CTACl:(8.5-47.0) TMAOH:(200-642) H2O. The presence of TMAOH is essential to maintain the gel pH at 8.5 or above. The pH greatly influences the nature of the final "crystalline" products, particularly the coordination of aluminum and phosphorus. XRD, EPMA, TEM, and N-2 adsorption measurements show that these solid products have a unique composition and disordered tubular mesopores with an average pore diameter of about 35 Angstrom in the calcined form. The overall P/Al ratio of UHM-1 is less than unity, especially in gels of higher pH, indicating incomplete condensation of phosphorus and a nonideal aluminophosphate framework. This may account for their poorer thermal stability relative to microporous aluminophosphate molecular sieves and aluminosilicate-based MCM-41 materials. Al-27 and P-31 MAS NMR reveal that aluminum in UHM-1 with a P/Al ratio of 0.60 synthesized at a gel pH of 8.5 is present in both tetrahedral and octahedral environments while phosphorus is present in a tetrahedral environment and also as hydroxylated species. As the P/Al ratio of UHM-1 decreases together with increasing gel pH, the relative amounts of tetrahedral aluminum and tetrahedral phosphorus decrease. This change suggests some Al-O-P linkages in the tetrahedral regions of the UHM-1 samples, and an increasing octahedral aluminum content st lower P/Al ratio indicates that octahedral aluminum alone can construct a tubular mesoporous structure. After incorporation of silicon into UHM-1, Si-29, Al-27, and P-31 MAS NMR of UHM-3 reveal that silicon is atomically dispersed and that the relative amounts of tetrahedral aluminum and tetrahedral phosphorus increase monotonically with increasing silicon incorporation. Virtually all the aluminum is tetrahedral, and all the phosphorus is tetrahedral after silicon incorporation reaches a Si/Al ratio of unity. This indicates more ordered atomic arrangements of tetrahedral silicon, aluminum, and phosphorus via oxygen bridges in UHM-3 than in UHM-1. The incorporation of silicon appears to make the aluminophosphate framework more flexible and facilitates the formation of an aluminophosphate-based mesoporous structure.

Characterization of Aluminophosphate-Based Tubular Mesoporous Molecular Sieves

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Tubular aluminophosphate mesoporous materials containing framework silicon, vanadium and manganese

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Synthesis of the Molecular-Sieve Alpo4-5 with an Unequal Molar Ratio of Al2o3 to P2o5

Multinuclear solid-state NMR studies on the formation mechanism of aluminophosphate molecular sieves in ionic liquids

Electron Spin Resonance And Electron Spin Echo Modulation Spectroscopy Of Aluminophosphate-Based Mesoporous Molecular Sieve Containing Framework Manganese

Synthesis and Characterization of Al-Msu-S Mesoporous and Meso-Microporous Molecular Sieves and Their Catalytic Performance

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Synthesis and characterization of a new mesoporous molecular sieve

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

Ionothermal Synthesis Process for Aluminophosphate Molecular Sieves in the Mixed Water/ionic Liquid System

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Synthesis and Characterization of AlMCM-41 Molecular Sieves

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Alumination and Ion Exchange of Mesoporous SBA-15 Molecular Sieves

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Pore structure of an aluminum phosphate molecular sieve