Abstract:series of aluminophosphate-based tubular mesoporous molecular sieves without (UHM-1) and with substituted silicon (UHM-3) have been synthesized at room temperature in the presence of a cationic surfactant cetyltrimethylammonium chloride (CTACl) and an organic base tetramethylammonium hydroxide (TMAOH). Characterization by powder X-ray diffraction (XRD), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), N-2 adsorption, and Al-27, P-31, and Si-29 magic-angle-spinning (MAS) NMR spectroscopies has been carried out to understand both the pore structures and the local atomic arrangements of these solid products. The synthesis of UHM-1 and UHM-3 is successful only at room temperature within the following molar gel composition: Al2O3:(0.6-3.4) P2O5:(0.0-1.0) SiO2:(0.24-0.50) CTACl:(8.5-47.0) TMAOH:(200-642) H2O. The presence of TMAOH is essential to maintain the gel pH at 8.5 or above. The pH greatly influences the nature of the final "crystalline" products, particularly the coordination of aluminum and phosphorus. XRD, EPMA, TEM, and N-2 adsorption measurements show that these solid products have a unique composition and disordered tubular mesopores with an average pore diameter of about 35 Angstrom in the calcined form. The overall P/Al ratio of UHM-1 is less than unity, especially in gels of higher pH, indicating incomplete condensation of phosphorus and a nonideal aluminophosphate framework. This may account for their poorer thermal stability relative to microporous aluminophosphate molecular sieves and aluminosilicate-based MCM-41 materials. Al-27 and P-31 MAS NMR reveal that aluminum in UHM-1 with a P/Al ratio of 0.60 synthesized at a gel pH of 8.5 is present in both tetrahedral and octahedral environments while phosphorus is present in a tetrahedral environment and also as hydroxylated species. As the P/Al ratio of UHM-1 decreases together with increasing gel pH, the relative amounts of tetrahedral aluminum and tetrahedral phosphorus decrease. This change suggests some Al-O-P linkages in the tetrahedral regions of the UHM-1 samples, and an increasing octahedral aluminum content st lower P/Al ratio indicates that octahedral aluminum alone can construct a tubular mesoporous structure. After incorporation of silicon into UHM-1, Si-29, Al-27, and P-31 MAS NMR of UHM-3 reveal that silicon is atomically dispersed and that the relative amounts of tetrahedral aluminum and tetrahedral phosphorus increase monotonically with increasing silicon incorporation. Virtually all the aluminum is tetrahedral, and all the phosphorus is tetrahedral after silicon incorporation reaches a Si/Al ratio of unity. This indicates more ordered atomic arrangements of tetrahedral silicon, aluminum, and phosphorus via oxygen bridges in UHM-3 than in UHM-1. The incorporation of silicon appears to make the aluminophosphate framework more flexible and facilitates the formation of an aluminophosphate-based mesoporous structure.

Tubular aluminophosphate mesoporous materials containing framework silicon, vanadium and manganese

Electron spin resonance and optical spectroscopy of tubular aluminophosphate materials containing framework vanadium

Electron Spin Resonance And Electron Spin Echo Modulation Spectroscopy Of Aluminophosphate-Based Mesoporous Molecular Sieve Containing Framework Manganese

Characterization of Aluminophosphate-Based Tubular Mesoporous Molecular Sieves

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Fabrication and Electrochemical Performance of Nanofibrous Micro-Frameworks of Α-Mno2

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

A novel method for synthesis of Co–Al layered double hydroxides and their conversions to mesoporous CoAl 2 O 4 nanostructures for applications in adsorption removal of fluoride ions

Synthesis of the Molecular-Sieve Alpo4-5 with an Unequal Molar Ratio of Al2o3 to P2o5

Synthesis and spectroscopic study of mesoporous aluminum methylphosphonate foam templated by dibutyl methylphosphonate

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

Mesoporous Aluminophosphates and Fe-Aluminophosphates with Highly Thermal Stability and Large Surface Area Templated from Semi-Fluorinated Surfactant

Hydrothermal synthesis and characterization of magnesium substituted aluminophosphate with unique intersecting 12-membered ring channels in three dimensions

Stable Tetrahedral Aluminum Sites in Hexagonal Mesoporous Aluminosilicates

A vesicle-aggregation-assembly approach to highly ordered mesoporous γ-alumina microspheres with shifted double-diamond networks.

Tetramethylguanidine-templated Synthesis of Aluminophosphate-Based Microporous Crystals with AFI-type Structure

Synthesis and Structural Characterization of the Aluminophosphate Molecular Sieve DPA-VPI-5

Solvothermal Synthesis and Characterization of a New 3-D Open Framework Aluminophosphate [Al2p3o12][c4n3h16]