Abstract:series of aluminophosphate-based tubular mesoporous molecular sieves without (UHM-1) and with substituted silicon (UHM-3) have been synthesized at room temperature in the presence of a cationic surfactant cetyltrimethylammonium chloride (CTACl) and an organic base tetramethylammonium hydroxide (TMAOH). Characterization by powder X-ray diffraction (XRD), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), N-2 adsorption, and Al-27, P-31, and Si-29 magic-angle-spinning (MAS) NMR spectroscopies has been carried out to understand both the pore structures and the local atomic arrangements of these solid products. The synthesis of UHM-1 and UHM-3 is successful only at room temperature within the following molar gel composition: Al2O3:(0.6-3.4) P2O5:(0.0-1.0) SiO2:(0.24-0.50) CTACl:(8.5-47.0) TMAOH:(200-642) H2O. The presence of TMAOH is essential to maintain the gel pH at 8.5 or above. The pH greatly influences the nature of the final "crystalline" products, particularly the coordination of aluminum and phosphorus. XRD, EPMA, TEM, and N-2 adsorption measurements show that these solid products have a unique composition and disordered tubular mesopores with an average pore diameter of about 35 Angstrom in the calcined form. The overall P/Al ratio of UHM-1 is less than unity, especially in gels of higher pH, indicating incomplete condensation of phosphorus and a nonideal aluminophosphate framework. This may account for their poorer thermal stability relative to microporous aluminophosphate molecular sieves and aluminosilicate-based MCM-41 materials. Al-27 and P-31 MAS NMR reveal that aluminum in UHM-1 with a P/Al ratio of 0.60 synthesized at a gel pH of 8.5 is present in both tetrahedral and octahedral environments while phosphorus is present in a tetrahedral environment and also as hydroxylated species. As the P/Al ratio of UHM-1 decreases together with increasing gel pH, the relative amounts of tetrahedral aluminum and tetrahedral phosphorus decrease. This change suggests some Al-O-P linkages in the tetrahedral regions of the UHM-1 samples, and an increasing octahedral aluminum content st lower P/Al ratio indicates that octahedral aluminum alone can construct a tubular mesoporous structure. After incorporation of silicon into UHM-1, Si-29, Al-27, and P-31 MAS NMR of UHM-3 reveal that silicon is atomically dispersed and that the relative amounts of tetrahedral aluminum and tetrahedral phosphorus increase monotonically with increasing silicon incorporation. Virtually all the aluminum is tetrahedral, and all the phosphorus is tetrahedral after silicon incorporation reaches a Si/Al ratio of unity. This indicates more ordered atomic arrangements of tetrahedral silicon, aluminum, and phosphorus via oxygen bridges in UHM-3 than in UHM-1. The incorporation of silicon appears to make the aluminophosphate framework more flexible and facilitates the formation of an aluminophosphate-based mesoporous structure.

Mesoporous Aluminophosphates and Fe-Aluminophosphates with Highly Thermal Stability and Large Surface Area Templated from Semi-Fluorinated Surfactant

A novel method for synthesis of Co–Al layered double hydroxides and their conversions to mesoporous CoAl 2 O 4 nanostructures for applications in adsorption removal of fluoride ions

Fluoride Ions Assistant Synthesis of Extremely Hydrothermal Stable Al-Sba-15 with Controllable Al Content

"Solvent-free" synthesis of thermally stable and hierarchically porous aluminophosphates (SF-APOs) and heteroatom-substituted aluminophosphates (SF-MAPOs)

A novel mesoporous silica-clay composite and its thermal and hydrothermal stabilities

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

Facile Synthesis for Ordered Mesoporous Gamma-Aluminas with High Thermal Stability

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Hydrothermally Highly Stable Acidic Mesoporous Aluminosilicate Spheres with Radial Channels

One-step synthesis of large pore mesoporous metallo-aluminophosphates under nonaqueous media

Synthesis of hydrothermally stable, hierarchically mesoporous aluminosilicate Al-SBA-1 and their catalytic properties

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Design and Synthesis of Ordered Mesoporous Silica Materials with High Degree of Silica Condensation at High Temperature from a Mixture of Polymer Surfactant with Small Organic Ammonium.

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Characterization of Aluminophosphate-Based Tubular Mesoporous Molecular Sieves

Hydrothermal Synthesis of High Surface Area Mesoporous Lithium Aluminate

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Mesoporous and Al-rich MFI Crystals Assembled with Aligned Nanorods in the Absence of Organic Templates