Abstract:Using tetraethylorthosilicate (TEOS), polymethylhydrosiloxane (PMHS) and aluminium isopropoxide (AIP) as the reactants, through a one-step nonsurfactant route based on PMHS–TEOS–AIP co-polycondensation, hydrothermally stable mesoporous aluminosilicates with different Si/Al molar ratios were successfully prepared. All samples exclusively showed narrow pore size distribution centered at 3.6nm. To assess the hydrothermal stability, samples were subjected to 100°C distilled water for 300h. The boiled mesoporous aluminosilicates have nearly the same N2 adsorption–desorption isotherms and the same pore size distributions as those newly synthesized ones, indicating excellent hydrothermal stability. The 29Si MAS NMR spectra confirmed that PMHS and TEOS have jointly condensed and CH3 groups have been introduced into the materials. The 27Al MAS NMR spectra indicated that Al atoms have been incorporated in the mesopore frameworks. The NH3 temperature-programmed desorption showed strong acidity. Due to the existence of large amount of CH3 groups, the mesoporous aluminosilicates obtained good hydrophobicity. Owing to the relatively large pore and the strong acidity provided by the uniform four-coordinated Al atoms, the excellent catalytic performance for 1,3,5-triisopropylbenzene cracking was acquired easily. The materials may be a profitable complement for the synthesis of solid acid catalysts.

Stable Tetrahedral Aluminum Sites in Hexagonal Mesoporous Aluminosilicates

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Ordered Mesoporous Aluminosilicates with Very Low Si/Al Ratio and Stable Tetrahedral Aluminum Sites for Catalysis

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Bifunctional Hybrid Mesoporous Organoaluminosilicates with Molecularly Ordered Ethylene Groups.

Hydrothermally Stable Ordered Hexagonal Mesoporous Aluminosilicates Assembled from A Triblock Copolymer and Preformed Aluminosilicate Precursors in Strongly Acidic Media

Synthesis, Characterization, and Catalytic Properties of Stable Mesoporous Aluminosilicates Assembled from Preformed Zeolite L Precursors

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Synthesis of ultrastable ordered mesoporous aluminosilicates molecular sieves with “hard template”

Synthesis of hydrothermally stable, hierarchically mesoporous aluminosilicate Al-SBA-1 and their catalytic properties

Creation Of Acid Sites On Sba-15 Mesoporous Silica By Alumination

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

High temperature synthesis of hydrothermally stable micro-mesoporous silica and Al-doped mesoporous silica via rigid template

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieve from Natural Halloysite

Hydrothermally Highly Stable Acidic Mesoporous Aluminosilicate Spheres with Radial Channels

A Stable Hexagonal Mesoporous Aluminophosphate Assembled from Preformed Aluminophosphate Precursors

Synthesis and characterization of ordered mesoporous aluminosilicates molecular sieves with highly hydrothermal stability

One-step synthesis of hydrothermally stable mesoporous aluminosilicates with strong acidity

Obtaining of Mesoporous Aluminosilicates with High Hydrothermal Stability by Composite Organic Templates: Utility and Mechanism

One-step Direct Synthesis of Mesoporous Aluminosilicates Al-SBA-15 with Cage-Like Macropores by Using Micrometer-Sized Aluminum Balls