Abstract:Ordered large-pore (up to 12 nm) and stable mesoporous aluminophosphates (AlPO) have been synthesized by using block copolymer (EO106PO70EO106, Pluronic F127) as a structure-directing agent. The selection of inorganic precursors is based on an “acid–base pair” route. Three acid–base pair, including AlCl3/H3PO4, AlCl3/OP(OCH3)3 and Al(OC4H9)3/PCl3 are confirmed to be efficient for the assembly of periodic mesoporous frameworks. Ordered 2-D hexagonal mesoporous aluminophosphates can be obtained by using AlCl3/H3PO4 as precursors, while disordered mesoporous aluminophosphates are produced by using AlCl3/OP(OCH3)3 or Al(OC4H9)3/PCl3 as precursors. BET surface areas and pore sizes of the products vary from 261 to 115 m2/g and from 9.4 to 12 nm, respectively. The solution and solid state 27Al and 31P MAS NMR were used to characterize the chemical environment of aluminium and phosphorus before and after the formation of mesostructured AlPO products, which simultaneously allows us to evaluate the efficiency of inorganic–inorganic (I–I) interactions (Al–O–P) of different acid–base pair. Both 27Al and 31P MAS NMR results show that among the three acid–base pair, AlCl3/H3PO4 pair interacts more readily with each other than the other two pairs [AlCl3/OP(OCH3)3, Al(OC4H9)3/PCl3], and tends to form rigid framework before calcination. The detailed structural characterizations reveal that strong I–I interactions (Al–O–P) between inorganic precursors will lead to a final mesoporous material with high structure regularity. This method can also be applied to synthesize iron-incorporated aluminophosphate (FeAlPO) with highly ordered 2-D hexagonal structure. BET surface area and pore size of FeAlPO prepared with Fe/Al=0.1 (molar ratio) are 181 m2/g and 8.9 nm, respectively. Electron spin resonance (ESR) and UV–vis spectra were employed to characterize the chemical state of Fe3+ ion.

A Stable Hexagonal Mesoporous Aluminophosphate Assembled from Preformed Aluminophosphate Precursors

Synthesis of Thermally Stable Mesoporous Hexagonal Aluminophosphate Molecular Sieves

Stable Tetrahedral Aluminum Sites in Hexagonal Mesoporous Aluminosilicates

Block Copolymer Templating Syntheses of Ordered Large-Pore Stable Mesoporous Aluminophosphates and Fe-aluminophosphate Based on an “acid–base Pair” Route

Stable Ordered Mesoporous Silica Materials Templated by High-Temperature Stable Surfactant Micelle in Alkaline Media

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Co‐templating Ionothermal Synthesis and Crystal Structure of a New Layered Aluminophosphate from a Protic Deep Eutectic Solvent

Vapor Phase Transport Synthesis and Structure Characterization of an Aluminophosphate Molecular Sieve [Al3P3O12F][C5H5NH]center dot 0.2H(2)O

Hydrothermally Stable Ordered Hexagonal Mesoporous Aluminosilicates Assembled from A Triblock Copolymer and Preformed Aluminosilicate Precursors in Strongly Acidic Media

Multinuclear solid-state NMR studies on the formation mechanism of aluminophosphate molecular sieves in ionic liquids

Synthesis of ordered mesoporous alumina with large pore sizes and hierarchical structure

A Novel Method for Synthesis of Co–Al Layered Double Hydroxides and Their Conversions to Mesoporous CoAl2O4 Nanostructures for Applications in Adsorption Removal of Fluoride Ions

Tubular aluminophosphate mesoporous materials containing framework silicon, vanadium and manganese

Synthesis, Characterization and Growth Mechanism of Hierarchical Cantaloupe-Like Alooh Superstructures by A Simple Hydrothermal Process

Strongly Acidic and High-Temperature Hydrothermally Stable Mesoporous Aluminosilicates with Ordered Hexagonal Structure

Hydrothermal Synthesis of High Surface Area Mesoporous Lithium Aluminate

Mesoporous Aluminophosphates and Fe-Aluminophosphates with Highly Thermal Stability and Large Surface Area Templated from Semi-Fluorinated Surfactant

Hexagonally ordered mesoporous ternary Li2O-TiO2-P2O5 oxides with high lithium content.

Synthesis of Highly Ordered Thermally Stable Cubic Mesostructured Zirconium Oxophosphate Templated by Tri-Headgroup Quaternary Ammonium Surfactants

Hydrothermally Highly Stable Acidic Mesoporous Aluminosilicate Spheres with Radial Channels

Controllable Syntheses of Hexagonal and Lamellar Mesostructured Lanthanum Oxide